1) high strength alloy steel
高强度合金钢
1.
The contrast cutting experiments have been carried out to research the cutting performance of turning the high strength alloy steel by using new developed Ni and Ni W based coating sintered carbide inserts and uncoated insert.
用新研制的Ni基、Ni W基涂层刀片与未涂层刀片进行了高强度合金钢的对比车削试验和切削性能研究 ,结果表明 ,新型涂层刀片切削性能良好 ,磨损较小 ,耐用度提高。
2.
Through the contrast cutting test of broaching the internal spiral keyslot of high strength alloy steel workpiece used broaches with and without coatings, the wear properties of broaches and the effect of re polishing rake face on cutting properties of broaches and the workpiece surface roughness are studied.
通过这两种涂层拉刀与未涂层拉刀的对比切削试验 ,研究了加工高强度合金钢内孔螺旋键槽时刀片的磨损性能及重磨前刀面对刀具切削性能和加工表面粗糙度的影响 ,并分析了提高涂层刀具寿命的机
2) Low-alloy high-strength steel
低合金高强度钢
1.
Based on question of developing low-alloy high-strength steel, strengthening mechanism of microalloy elements in the steel was approached.
针对国内低合金高强度钢发展中存在的问题 ,探讨了该钢种微合金元素的强化机理 ,简要介绍了低合金高强度钢的成分的优化设计及生产工艺。
3) HSLA Steel
高强度低合金钢
1.
Some means increasing strength and the theory of grain refinement in HSLA steel are discussed.
为高强度低合金钢组织超细化技术的理论研究和实际工程应用提供参考。
4) HSLA
低合金高强度钢
1.
Thermodynamics of Carbide and Nitride Precipitation in HSLA Steel;
低合金高强度钢中氮化物和碳化物析出热力学
2.
Developing HSLA Steels and Promoting Change of Growing Manner of Chinese Steel Industry;
大力发展低合金高强度钢促进钢铁工业增长方式的转变
3.
The microstructures and tensile properties of HSLA in different relaxation times were studied.
研究了低合金高强度钢在不同弛豫时间下的组织和拉伸性能。
6) HSLA steel
低合金高强度钢
1.
Base on regular solution model and traditional nucleation theory, carbo-nitride precipitation model in austenite of HSLA steel during continuous cooling process is developed.
采用规则溶液描述低合金高强度钢奥氏体相中碳氮化物的热力学性质,以经典形核理论为基础,建立了低合金高强度钢奥氏体相中碳氮化物在连续冷却过程中碳氮化物析出模型。
2.
The effects of welding cooling time and heat temperature on fracture toughness and microstructure feature for an 800MPa grade HSLA steel and heat affected zone(HAZ) were investigate using thermal simulation specimens.
随着工程机械的大型化,需要采用800MPa低合金高强度钢结构。
3.
The microstructures and tensile properties of HSLA steel in different relaxation time were studied.
低合金高强度钢在不同驰豫时间下具有组织与拉伸性能。
补充资料：低合金超高强度钢
低合金超高强度钢
low alloy ultra high-strength steel
夹杂物的数量，从而提高大截面棒材的横向断面收缩率和断裂韧度。按照实际需要和条件，生产低合金超高强度钢多采用下列四种冶炼工艺，即电弧炉加电渣重熔;电弧炉加真空自耗;真空感应炉加电渣重熔和真空感应炉加真空自耗冶炼。 表2 40CrNiZSiZMovA钢中气体含里操华操门阵 表3 40erNiZSiZMovA钢的横向力学性能默介斗 (2)锻、轧加工。低合金超高强度钢具有良好的热加工变形性能，可在900~1150℃范围内进行锻造和轧制。钢的过热敏感性小，加热过程不易产生过热和过烧现象。终止加工变形温度一般控制在850C以上。钢锭经锻压成材的最小锻压比应不小于5。对于要求横向塑性指标的锻件采用多次辙粗和拔长变形工艺，以改善钢的横向性能。锻后和轧后钢材应进行退火或正火加高温回火，获得均匀的显微组织，为切削加工和最终热处理做好准备。 中碳低合金超高强度钢在轧制前加热和退火热处理时容易产生表面脱碳现象，从而造成钢板强度降低、疲劳强度极限下降;严重影响钢的使用，为了防止脱碳，板材特别是薄板应在保护气氛条件下进行退火处理。如条件不具备时，应严格控制退火温度和保温时间，尽量减少因表面脱碳对板材造成不良影响。 (3)焊接。低合金超高强度钢的焊接性主要取决于钢中碳和合金元素的含量。碳含量大于。.35%时，其焊接性恶化。碳含量愈高，其焊接性愈差。主要是因为焊缝和热影响区在焊后空冷形成粗大马氏体组织，容易产生微裂纹。应采用低碳低含氢量高纯度焊丝或焊条焊接。并且在焊前经200一35oC预热，焊后及时进行缓冷和高温回火处理。 (4)表面防护。低合金超高强度钢制作的结构部件对表面缺陷的敏感性较高。在受力条件下，表面缺陷处产生应力集中，因而就容易发生结构件的疲劳破坏或者应力腐蚀延迟断裂。因此，改善结构件表面精度和状态是提高疲劳寿命的有效措施。通常采用表面喷丸强化工艺使零部件表面层形成残余压应力，并使表层晶粒细化，增加位错密度，提高表层屈服强度，降低表面缺陷的有害影响，从而改善和提高零件的疲劳强度，延长使用寿命。如4oCrNiZMoA钢制作的结构件，经喷丸强化后，表层残余压应力达到700~8。。MPa，与不喷丸的零件相比，其疲劳强度提高了40%以上。d lhej}n ehoogaoq旧ngdugong低合金超高强度钢(low alloy ultra high-strcngth steel)合金元素总含量在5%以下，经热处理后的屈服强度大于138OMPa的超高强度钢。钢的强度主要取决于其含碳量。通过淬火加低温回火或等温淬火热处理获得回火马氏体或回火马氏体加贝氏体显微组织以获得高强度和良好的塑性与韧性。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。