说明:双击或选中下面任意单词,将显示该词的音标、读音、翻译等;选中中文或多个词,将显示翻译。
您的位置:首页 -> 词典 -> 250℃人工时效
1)  artificial aging at250℃
250℃人工时效
2)  aging [英]['eidʒiŋ]  [美]['edʒɪŋ]
人工时效
1.
Solid Solution Treatment and Artificial Aging of Mg-Al-Mn-RE Alloy;
Mg-Al-Mn-RE合金固溶处理和人工时效研究
2.
The results are as follows: Microstructure of artificial aging and seasoning are both α(Al) matrix,Sn-phase and compounds;compared with the seasoning of TZS88 alloy,the tensile strength of the alloy using manual aged process increases by around 5 percent,and the hardness increases by 0.
研究了自然时效和人工时效状态下新型铝基合金TZS88的性能,且通过金相显微镜、扫描电镜对其时效组织进行了分析。
3)  aging treatment
人工时效
1.
In this paper,the microstructure and mechanical properties of 6063 Al alloy at different aging temperature and time has been studied The research results showed that the aging process(175℃×1 5h+200℃×3h)is available to obtain higher hardness of thin walled fashioned alloy Its hardness can reach over 75HV after aging treatmen
分析了6063铝合金人工时效时的组织结构变化,研究了不同的时效温度和时效时间对6063铝合金力学性能的影响。
4)  artificial ageing
人工时效
1.
The production process institutions of 6005A-T6 aluminium alloy sheet and plate were determined as following: the quenching temperature is 520℃,the temperature and time of artificial ageing is(165±5)℃ 8 h.
研究了6005A铝合金板材淬火温度、人工时效温度和时间与板材组织、性能的关系,确定了6005A-T6板材的热处理制度:淬火温度520℃,人工时效温度及时间为(165±5)℃8 h。
2.
Effects of artificial ageing on the hardness distributions and strength were analyzed for 6063 aluminum alloy joints welded by varying heat inputs.
对不同焊接热输入下的6063铝合金焊接接头进行人工时效,分析其硬度分布和强度的变化。
3.
By artificial ageing,the grain boundaries could be appeared while the grain size is kept unchanged.
研究了01420合金焊缝金属析出相的分布规律、结晶类型及晶粒度之间的内在联系,通过人工时效处理,使该合金焊缝金属在保持焊后态晶粒度不变的前提下,经腐蚀后显现晶界。
5)  artificial aging
人工时效
1.
Microstructure and properties of 2B16 aluminum alloy electron beam welding joints after artificial aging
人工时效后2B16铝合金电子束焊接接头的组织与性能
2.
The effects of artificial aging on mechanical properties and damping capacity of ZA84 magnesium alloy with rare earth element (RE) were studied.
研究了人工时效对RE变质ZA 84镁合金力学性能及阻尼性能的影响。
3.
The microstructures and tensile properties of artificial aging and natural aging a new aluminum matrix sliding bearing alloy TZS88 were investigated by SEM,metallograph analysis,hardness and tensile tests.
通过金相显微镜、扫描电镜观察、硬度和拉伸试验研究了自然时效和人工时效状态下新型铝基合金TZS88的组织与性能。
6)  artificial age
人工时效
补充资料:人工时效

artificialaging:将钢材或工件在高于室温下长期停留并产生组织和性能变化的过程。

说明:补充资料仅用于学习参考,请勿用于其它任何用途。