1) nanocrystal MnZn ferrite particle
锰锌铁氧体纳米晶
1.
Single phase aggregate-free nanocrystal MnZn ferrite particles with a size of 10~20nm were perapared via hydrothermal method by additive, which were characterized by TEM and XRD.
通过加入添加剂经水热合成法制备了单相无硬团聚的 10~ 2 0nm锰锌铁氧体纳米晶 ,运用TEM ,XRD等进行了表征。
2) ZnMn ferrite nanoscale particles
锌锰铁氧体纳米晶
3) manganese copper zinc nanocrystalline ferrite
锰铜锌纳米晶铁氧体
4) nano-sized Mn-Zn ferrite powders
纳米锰锌铁氧体
1.
Based on the precursor of ZnSO 4 ·7H 2 O,FeCI 3 ·6H 2 O and MnSO 4 ,nano-sized Mn-Zn ferrite powders were synthesized by the catalysis of Fe 2+ in boiling circumfluence.
以ZnSO4·7H2O,FeCl3·6H2O和MnSO4为原料,采用液相沸腾回流法,成功地制备出了纳米锰锌铁氧体。
5) MnZn ferrite nanocrystal
锰锌铁氧体纳米粉体
1.
The MnZn ferrite nanocrystal has been successfully synthesized by a simple synthesis, co-precipitation phase transformation.
本文采用的软磁锰锌铁氧体纳米粉体,是用一种简单的方法,即共沉淀沸腾回流相转化法制备的。
6) ZnCo ferrite nanoparticle
锌钴铁氧体纳米晶粒
补充资料:锰-锌铁氧体
分子式:Mn-Zn
CAS号:
性质:软磁铁氧体的主要品种之一。具有尖晶石型结构。密度5.1g/cm3,维氏硬度600~800。初始磁导率ua1000~5000。磁导率与品质因素的乘积150000(100kHz)。居里点134~200℃。饱和磁感应强度0.3~0.5T。矫顽力8~36A/m。电阻率20~1000Ω·cm。主要原料为铁、锰、锌的氧化物或盐类。一般用电子陶瓷工艺制造。如采用控制气氛烧结或热压烧结等新工艺,可获得性能优良的产品。一般在1kHz~10MHz频率范围内使用。可用于制作电感器、脉冲变压器、滤波器的磁芯、介质天然及磁头等。
CAS号:
性质:软磁铁氧体的主要品种之一。具有尖晶石型结构。密度5.1g/cm3,维氏硬度600~800。初始磁导率ua1000~5000。磁导率与品质因素的乘积150000(100kHz)。居里点134~200℃。饱和磁感应强度0.3~0.5T。矫顽力8~36A/m。电阻率20~1000Ω·cm。主要原料为铁、锰、锌的氧化物或盐类。一般用电子陶瓷工艺制造。如采用控制气氛烧结或热压烧结等新工艺,可获得性能优良的产品。一般在1kHz~10MHz频率范围内使用。可用于制作电感器、脉冲变压器、滤波器的磁芯、介质天然及磁头等。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。