1) biax orientation polyester film
双向拉伸聚酯薄膜
1.
In this paper,behavior of thermal expansion heat shrinkage of biax orientation polyester film was studied by thermo mechanical analysis(TMA).
应用热机械分析考察双向拉伸聚酯薄膜的热膨胀—收缩行为 ,表明其与成膜工艺 ,尤其是与热定型工艺之间有一定的相关
2) biaxially oriented polypropylene film
双向拉伸聚丙烯薄膜
1.
By analyzing the steam system of MDO and TDO of Fushun biaxially oriented polypropylene film(BOPP)production line,a technical reformation project of steam step utilization in order to improve the existing process was proposed.
通过对抚顺石化20 kt/a 双向拉伸聚丙烯薄膜(BOPP)生产线纵向拉伸和横向拉伸蒸汽系统的分析,探讨了蒸汽梯级利用的技术改造方案,对原设计流程加以改进。
3) BOPP film
双向拉伸聚丙烯薄膜
1.
It introduced the present situation of the BOPP film in China and looked forward to its development trend.
介绍了我国双向拉伸聚丙烯薄膜的市场现状,并对其发展趋势进行了展望。
2.
The slipping of BOPP film in winding the elecment for capacitor is one of the key factors affecting the manufacturing quality of capacitors.
电容器用双向拉伸聚丙烯薄膜的打滑现象 ,是影响薄膜电容器制造质量的关键因素之一。
4) biaxially oriented polyamide film
双向拉伸聚酰胺薄膜
6) Biaxially oriented polypropylene (BOPP) film
双向拉伸聚丙烯薄膜(BOPP)
补充资料：聚酯薄膜
分子式：
CAS号：
性质：系指由聚对苯二甲酸乙二酯经双向拉伸制得的薄膜。具有坚韧、耐寒、化学稳定性、尺寸稳定性和电性能好的特点。可在120℃长期使用，150℃短期使用，-100℃以下仍有柔性。拉伸强度117～173MPa，是聚乙烯膜的9倍，PC膜的3倍；断裂伸长率50％～130％；体积电阻率1021Ω·cm，介电常数(106Hz)2.98。先将树脂挤成薄片，再经双向拉伸制得。主要用作电影胶片、X光片基、录音录像带基、电机绝缘和电容器膜、重包装膜和生产增强聚酯波纹板的隔离膜等。
CAS号：
性质：系指由聚对苯二甲酸乙二酯经双向拉伸制得的薄膜。具有坚韧、耐寒、化学稳定性、尺寸稳定性和电性能好的特点。可在120℃长期使用，150℃短期使用，-100℃以下仍有柔性。拉伸强度117～173MPa，是聚乙烯膜的9倍，PC膜的3倍；断裂伸长率50％～130％；体积电阻率1021Ω·cm，介电常数(106Hz)2.98。先将树脂挤成薄片，再经双向拉伸制得。主要用作电影胶片、X光片基、录音录像带基、电机绝缘和电容器膜、重包装膜和生产增强聚酯波纹板的隔离膜等。