1) nonylphenolic resin
壬基酚醛树脂
1.
Rosin modified nonylphenolic resin was synthesized by one - step synthesis in laboratory.
在实验室内用一步法合成了松香改性壬基酚醛树脂。
2) octylphenolic resin
辛基酚醛树脂
1.
The alkyd modified t-octylphenolic resin was prepared by alcoholized linseed oil with pentaerythritol,rosin and octylphenolic resin.
亚麻油用季戊四醇醇解后与松香对辛基酚醛树脂进行改性合成了醇酸改性辛基酚醛树脂。
3) Anino-novolac resin
胺基酚醛型树脂
4) multicarboxyl phenolic resin
多羧基酚醛树脂
6) sulfomethyl phenol formaldehyde resin
磺甲基酚醛树脂
1.
Using phenol ,formaldehyde,sodiumhydrogensulfite and sodeum sulfite,a liner highmolecular comound,the sulfomethyl phenol formaldehyde resin was synthesised by means of condensation polymerization and addition polymerization,which is a good additive in slurry of deep oil well.
用苯酚、甲醛、亚硫酸氢钠、亚硫酸钠为主要原料 ,在一定条件下 ,经加成聚合和缩合聚合制得具有线型结构的高分子化合物———磺甲基酚醛树脂 ,它是油田深井泥浆的良好添加剂。
2.
The influences of different sulfonated lignite as compatible material on quality estimation of sulfomethyl phenol formaldehyde resin(SMP) were analyzed by experiments.
实验分析了作为配伍材料的磺化褐煤对磺甲基酚醛树脂质量评价的影响。
补充资料：2401纯酚醛树脂
2401树脂是由烷基苯酚和甲醛在碱性介质下缩聚而制得。有优良的耐热性、耐磨性、耐水性和耐老化性等。溶于苯、甲苯、醋酸乙酯、溶剂汽油、环己烷等有机溶剂和植物油。240l树脂的质量规格与2402完全相同。与氯丁橡胶和丁腈橡胶有良好的相容性。
外观 黄色至棕红色透明块状固体
软化点(环球法) 80-110 ℃
油溶性(树脂：桐油＝1：2) 全溶
用作氯丁胶粘剂的增粘树脂，以该树脂配制的氯丁溶剂型胶粘剂，粘接铝帆布的剥离强度达4kN／m。还可用作压敏胶的增粘剂、丁基橡胶的硫化剂等。贮存于阴凉、通风的库房内，远离火种、热源。
外观 黄色至棕红色透明块状固体
软化点(环球法) 80-110 ℃
油溶性(树脂：桐油＝1：2) 全溶
用作氯丁胶粘剂的增粘树脂，以该树脂配制的氯丁溶剂型胶粘剂，粘接铝帆布的剥离强度达4kN／m。还可用作压敏胶的增粘剂、丁基橡胶的硫化剂等。贮存于阴凉、通风的库房内，远离火种、热源。