1) apparent crystallization energy
晶化表观激活能
2) Apparent crystallization activation energy
晶化表观激话能
3) apparent activation energy
表观激活能
1.
The value of apparent activation energy increases at first with the i.
研究了Ti40合金在室温、300、500和600℃下的疲劳裂纹扩展行为,计算了Ti40合金在300、500、600℃下当△K为20MPam1/2时与裂纹扩展密切相关的表观激活能。
4) activation energy
表观激活能
1.
The activation energy (ΔE) at the glass transition temperature was much smaller than tradition amorphous alloys and have different magnitude compared to ΔE value at T x.
分析结果表明 :玻璃转变表观激活能越小 ,则晶化转变激活能越大 ,表现出相反的难易程度 ,且玻璃转变表观激活能数值远较传统非晶要小 ,验证了大块非晶合金独特的结构特点及玻璃形成能力 (GFA)强的原因 。
5) activation energy
晶化激活能
1.
The experimental results show that the crystallization temperature( T p) and activation energy ( E c) of the crystalline phases ( α Fe and Sm 2Fe 17 C x ) can be decreased going through pre annealing, the trend of activation energy change of α Fe phase can be changed in the crystallization process, which is helpful to formati.
结果表明 ,预退火处理使非晶合金晶化相α Fe和Sm2 Fe17Cx 的晶化温度 (Tp)和晶化表观激活能(Ec)值降低 ,且改变晶化相α Fe在晶化过程中晶化激活能的变化趋势 ,有助于该合金在晶化退火中形成晶粒尺寸较小的α Fe相。
2.
The activation energy of glass transition,crystallization and peak crystallization are 390.
2kJ/mol、晶化激活能Ex为325。
6) crystallization activation energy
晶化激活能
1.
The crystallization activation energy has been calculated by DTA and Kissinger equation.
非晶态合金Fe78Si9B1 3样品经短时超短脉冲电流处理 ,发生了结构弛豫 ,用DTA方法及Kissinger方程计算非晶样品的晶化激活能 ,用穆斯堡尔谱学方法研究了试样在电脉冲处理后的无反冲分数的变化 。
2.
The apparent crystallization activation energy E, is calculated to be 471.
采用Kissinger和Doylle-Ozawa方法计算了表观晶化激活能E_a,分别为471。
3.
The crystallization activation energy calculated by the onset crystallization temperatures decreases obviously.
Nb使由初始晶化温度计算的晶化激活能明显降低。
补充资料：表观活化能
分子式：
CAS号：
性质：当某复杂的总反应其表观速率常数k与温度T的关系符合阿伦尼乌斯公式k=A·e-Ea/RT时，其活化能Ea。称为该总反应的表观活化能。式中A及R分别为表观指前因子及摩尔气体常数。
CAS号：
性质：当某复杂的总反应其表观速率常数k与温度T的关系符合阿伦尼乌斯公式k=A·e-Ea/RT时，其活化能Ea。称为该总反应的表观活化能。式中A及R分别为表观指前因子及摩尔气体常数。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。