1) maximum drawing load
最大拉深力
1.
Orthogonal experimentswere carried outto investigate the main technologicalfactorsinfluencing the maximum drawing load in cup- drawing and the following conclusions were drawn:the most notable factor to affect the maximum drawing load is the type of lubricants and the second is the radius of the die arc,then the blank- holder pressure and the radius of the punch arc.
应用正交试验法研究影响杯形件最大拉深力的主要工艺因素 。
2.
Through the medium of simulating and technical test,traditional views on the happening time of maximum drawing load is verified.
通过数值模拟与工艺试验,验证了最大拉深力出现时刻的传统观点,但对其破裂问题有新的补充发现;提出了拉深破裂位置的一种新认识;并描述了拉深破裂发生时的一些规律及力学特点。
2) Maximum pulling force
最大拉力
3) Maximum static pull force
最大静拉力
4) maximum tension stress
最大拉应力
5) maximum penetration depth
最大测深能力
1.
The relationship between parameters of airborne laser bathymetry (ALB) and its maximum penetration depth is discussed.
以确定的参量建立的系统具有白天 4 9m和晚上 6 5m的最大测深能力 ,可完全满足在沿岸带以及岛礁的测量要
6) maximal radial stress
最大径向拉应力
1.
Through the differential expression,the variation of maximal radial stress in flange region for circle sheet drawing is discussed and compared with the method by qualitative explanation.
文章通过微分表达形式,对拉深凸缘最大径向拉应力的变化及其影响因素进行了分析论证,并与目前通用的直接对最大径向拉应力公式作定性解释的方法作了比较。
补充资料：各种材料拉深时的单位压边力数据
在单动压力机上拉深时的单位压边力
材 料 | q/MPa |
铝 | 0.8～1.2 |
紫铜,杜拉铝(退火的或刚淬火的) | 1.2～1.8 |
黄铜 | 1.5～2.0 |
压轧青铜 | 2.0～2.5 |
20钢、08钢、镀锡钢板 | 2.5～3.0 |
软化耐热钢 | 2.8～3.5 |
高合金钢,高锰钢,不锈钢 | 3.0～4.5 |
在双动压力机上拉深时的单位压边力
工件复杂程度 | q/MPa |
难加工件 | 3.7 |
普通加工件 | 3.0 |
易加工件 | 2.5 |
材 料 | 单位压边力q/MPa |
铝(退火状态) | 0.8～1.2 |
铝(硬态) | 1.2～1.4 |
黄铜(退火状态) | 1.5～2.0 |
黄铜(硬态) | 2.4～2.6 |
铜(退火状态) | 1.2～1.8 |
铜(硬态) | 1.8～2.2 |
康铜BMn40-1.5(硬态) | 2.6～2.9 |
可伐合金4J29(退火状态) | 3.0～3.3 |
钼(退火状态) | 4.0～4.5 |
软钢t＜0.5mm | 2.5～3.0 |
软钢t＞0.5mm | 2.0～2.5 |
不锈钢1Cr18Ni9Ti | 4.5～5.5 |
镍铬合金Cr20Ni80 | 3.5～4.0 |
说明：补充资料仅用于学习参考，请勿用于其它任何用途。