1) loose medium
疏松介质
2) porosity
疏松
1.
Effect of electric current pulse on shrinkage cavity and porosity in casting ZA27 alloy;
脉冲电流对铸造ZA27合金中缩孔和疏松的影响
2.
Factor Analysis and Countermeasures of Porosity and Pipe in Ingot;
钢锭疏松、缩孔的因素分析及对策
3.
In this paper, analysis on the fissuring accident of ZGMn13Cr2Mo antifriction tup is performed, and the reason is believed to lie in serious casting defects of shrinkage cavity, porosity and inclusion.
对ZGMn13Cr2Mo耐磨锤头的断裂事故进行了分析,主要原因是存在着严重的铸造缺陷:缩孔、疏松和夹杂物。
3) Looseness
疏松
1.
Results indicate that the primary cause to the rupture of the screw in the process of torque force test is proved to be heavily existence of holes and pore gaps in the screw arising from the central looseness of the original billet.
结果得出:螺钉在扭力试验过程中断裂是由于内部存在严重的孔洞和孔隙所造成的,孔洞和孔隙来源于原铸坯的中心疏松。
2.
Mechanism of central parosity and looseness of small billet is described and analysed.
简述小方坯中心缩孔和疏松的形成机理 ,提出减轻中心缩孔和疏松的措
3.
The experimental results show that there are some internal metallurgy flaws such as looseness,shrink hole in the raw material of the axle,and bad widmanstatten structure from the overheating and over-burning during the heating of forging,the comprehensive effects of these factors cause the steel toughness to reduce,and the internal cleavage exists d.
结果表明,车轴轴头原材料中存在疏松、缩孔残余等内部冶金缺陷和锻造热加工中的过热和过烧产生不良的魏氏组织,这些因素的综合作用致使钢的韧性降低,在锻造中发生内部劈裂,最终造成轴头在受外力时脆性断裂。
4) porous
疏松
1.
A new heterogeneous polymerization process, in which water acted as a dispersed phase and methyl methacrylate (MMA) as a continuous phase, was developed to prepare porous poly(methyl methacrylate) (PMMA) resin.
以水为分散相、甲基丙烯酸甲酯(MMA)为连续相进行悬浮态乳液聚合,合成疏松型聚甲基丙烯酸甲酯(PMMA)树脂。
5) shrinkage porosity
疏松
1.
Mold-filling, solidification and prediction of shrinkage porosity in Ti-46%Al alloy investment were performed using the ViewCast code, and the defects observed in the actual products agree well with the simulated results.
应用铸造软件ViewCast模拟精密铸造Ti 46%Al合金叶片的充型与凝固过程,预测了疏松的形成,模拟结果与实验结果相吻合。
6) loose
疏松
1.
Vibroflotation compaction is a comparably mature method for the improvement of cohesiveless soils,but it is seldom used to strengthen loose silty fine sands,especially for depth over 15m.
结合上海市某重点工程,基于吹填粉细砂的工程特性,通过现场试验探索出振冲工艺的主要设计和施工参数,对深度15m以上的饱和疏松粉细砂地基采用振冲加固的有效性进行了现场试验研究。
2.
They are as following: there is loose defect on the inner side,at the same time ther.
本文对开裂的阀体取样进行了化学成分、力学性能和金相组织的测定,找出了造成ZG20CrMoV阀体打水压断裂的主要原因是内部有疏松缺陷,内表面有沿着疏松长十几毫米的裂纹,再加上塑性和韧性都低,造成了最终打水压时的开裂。
参考词条
补充资料：钢锭疏松
钢锭疏松
shrinkage porosity
gangd旧9 shusong钢锭疏松(shrinkage porosity)镇静钢钢锭内部的微小孔隙。集中分布于轴心区的微小孔隙称中心疏松，分散于其他部位的微小孔隙称一般疏松。疏松一般通过钢坯或钢材的横向酸蚀试样检验。疏松程度根据标准评级图评定，分为1级至5级。疏松破坏钢组织的致密性，降低钢的塑性和韧性。对于内部致密度要求严格的合金钢及优质碳素结构钢，技术标准规定疏松应小于2级或3级。钢锭疏松是由于钢锭凝固过程中某些微小封闭区域钢液冷凝收缩得不到填充所致。收缩倾向大的钢种，疏松程度亦大。疏松通常与偏析伴生。钢中气体、非金属夹杂及硫、磷等杂质元素含量高时，疏松程度加重。选择合理的锭型，提高钢液的纯净度，控制适宜的注温、注速，有利于减轻疏松程度。增大钢锭轧制的压缩比，可显著降低疏松评级和减弱其不良影响。 (颜广庭)