1) high speed warm extrusion
高速温挤压
1.
The technological specification of the pole by the high speed warm extrusion was worked out.
拟制了磁极高速温挤压工艺规范。
2) high temperature extrusion
高温挤压
3) high speed extrusion
高速挤压
1.
Give a detail elaborate on advanced techniques such as the isothetmal extrusion , high speed extrusion, optimizing extrusion process parameters, autonatic control systems, treating as a reference to development of product for Chinese enterprise.
介绍和分析了国外硬钎料挤压技术的现状，阐述了等温挤压、高速挤压、挤压工艺参数优化及自动控制系统等先进技术，供国内企业发展生产参考。
2.
The article describes the technical development of aluminium extrusion presses in the world with respect to the process technology, mechanic equipment, hydraulic and automatic control systems with special stresses on describing the advanced techniques such as the isothermal extrusion, high speed extrusion, optimizing extrusion process parameters, indirect extrusion and etc.
介绍了国外挤压机在工艺、机械、液压和自动控制方面的技术发展，着重叙述等温挤压、高速挤压、挤压工艺参数优化和反向挤压等先进技术以及为实现等温挤压和高速挤压所采取的铸锭梯温加热、挤压减速控制、模具冷却等措施。
4) high-speed cold extrusion
高速冷挤压
1.
Technological measures for prolonging the life of high-speed cold extrusion terrace dies was extracted from production practice.
从生产实践中总结出延长高速冷挤压凸模使用寿命的有关工艺措施，并对其作用机理进行了理论分析。
5) high-speed extrusion at low temperature
低温快速挤压
6) extrusion forming
高温挤压成型
补充资料：温挤压
温挤压
warm extrusion
WenllyO温挤压(warm extrusion)将锭坯加热到回复温度以上再结晶温度以下进行的挤压。钢的温挤压温度范围高于室温而低于800~840℃，铝及铝合金的是从室温到250℃，铜及铜合金的是从室温到350℃，即基本上处于金属的不完全冷变形与不完全热变形的温度范围。 与热挤压和冷挤压相比，温挤压时锭坯的变形抗力比冷挤压时要小，成形比冷挤压容易，所需压力机的吨位可以减小。若控制合适，模具的寿命比冷挤压时要长，产品的性能也比退火材料要高，产品尺寸精度与粗糙度比热挤压的好。 温挤压既可用于生产有色金属制品，也可用于生产钢材，还可用于制造带型腔的模具。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。