1) composite coating with Cr Si Al
Al-Si-Cr复合涂层
2) Cr-Al-Si coating
Cr-Al-Si涂层
1.
Preparation of SiC/Cr-Al-Si coating for C/C composites by two-step pack cementation method
两步包埋法制备C/C复合材料SiC/Cr-Al-Si涂层研究
3) Ni-Co-Cr-Al-Y-Si-B coating
Ni-Co-Cr-Al-Y-Si-B涂层
1.
Ni-Co-Cr-Al-Y-Si-B coatings were deposited on Ni base superalloys DZ125 and DSM11 by arc ion plating (AIP).
采用电弧离子镀技术在DZ125和DSM11两种镍基高温合金基材上沉积Ni-Co-Cr-Al-Y-Si-B涂层,研究了高温合金基材及其Ni-Co-Cr-Al-Y-Si-B涂层在900℃的75％Na2SO4+25％K2SO4熔盐中的热腐蚀行为。
5) Al-Cr alloy coating
Al-Cr合金涂层
6) Al-Si coating
Al-Si涂层
1.
Research on corrosion resistance of an Al-Si coating on a K4104 high-temperature alloy;
K4104高温合金Al-Si涂层耐腐蚀性能研究
2.
Al-Si coatings were prepared on the superalloy K4104 by the slurry process.
用无机盐料浆法在K4104镍基高温合金表面制备了渗Al-Si涂层。
3.
Al-Si coating were prepared on nickel-base superalloy ЖС6У by molten slurry process.
用熔烧型料浆法在镍基高温合金ЖС6У表面制备了Al-Si涂层。
补充资料：等离子喷涂羟基磷灰石涂层-钛复合材料
分子式：
CAS号：
性质：是用等离子喷涂技术在医用金属钛或其合金表面加涂羟基磷灰石所制得的医用涂层材料。主要用于承力部位的硬组织修复和替换，如制作人工种植牙、关节柄和接骨板等。由于表面涂层赋予了表面生物活性，植入骨内后能与骨直接形成骨键合，手术中可不用骨水泥固定。为使涂层能在生物环境中保持稳定和涂层-基体界面具有足够的结合强度，要求涂层的羟基磷灰石含量达90％以上并具有高的结晶度。另外，钴基合金也可作为这种涂层材料的基材。
CAS号：
性质：是用等离子喷涂技术在医用金属钛或其合金表面加涂羟基磷灰石所制得的医用涂层材料。主要用于承力部位的硬组织修复和替换，如制作人工种植牙、关节柄和接骨板等。由于表面涂层赋予了表面生物活性，植入骨内后能与骨直接形成骨键合，手术中可不用骨水泥固定。为使涂层能在生物环境中保持稳定和涂层-基体界面具有足够的结合强度，要求涂层的羟基磷灰石含量达90％以上并具有高的结晶度。另外，钴基合金也可作为这种涂层材料的基材。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。