2) catalytic membrane
催化膜
1.
A catalytic membrane,supported on porous titanium plate,composed of heteropoly compound(H_(x)Cu_(1.
5O2分别制成催化膜,在特制的膜催化反应器中进行异丁烯选择氧化反应。
2.
The solubility of catalytic membrane of PVA-Zr(Ⅳ) was investigated and that the catalytic layer was found to swell in nearly two hours.
比较了PVA Zr (Ⅳ )催化膜和无催化活性层的PVA膜渗透性
3.
A catalytic membrane, supported on porous titanium plate, composed of heteropoly compound (H x Cu 1.
6Mo12 Oy的杂多化合物与具有氧溢流效应的氧化物Sb2 O4 制成催化膜 ,在特制的膜催化反应器中进行异丁烯选择氧化反应 。
3) Catalytic film
催化膜
1.
Catalytic film combustion is one of the most effective methods for environment protection and energy conservation, in which the catalysis metal is coated on the quite thin support, and the gas fully mixed with air is ignited and burned on the support without flame.
催化膜燃烧技术是将具有催化性能的金属加载在较薄的催化剂载体上,将与空气充分混合的天然气 点燃后在载体上进行无焰燃烧,载体上温度分布比较均匀,燃烧中产生的NOx含量很低,甚至接近零排放,是环保 与节能的一种有效方法。
4) film photocatalyst
光催化膜
1.
This paper describes the preparation of TiO2 film photocatalyst fixed on the oxygen-diffusion film .
本文提出用氧扩散膜作ＴｉＯ２光催化膜的载体，介绍了氧扩散膜的制备及ＴｉＯ２在氧扩散膜表面的固定方法，ＴｉＯ２光催化膜的表面形态与微结构，不同条件下光催化分解草酸的速度。
5) Membrane catalyst
膜催化剂
1.
γ-Al2O3 coating was coated on the surface of theα-Al2O3 ceramic tube to prepareγ-Al2O3 modified ceramic support which was used to prepare membrane catalysis, then Pd-Ag bimetallic membrane catalysts which contains 25% Ag, 50%Ag and 75% respectively, and Pd-Ag-Pt, Pd-Ag-Au trimetallic membrane catalysts were prepared on the surface of ceramic tubes modified byγ-Al2O3 coating.
在α-Al2O3基体膜管上涂γ-Al2O3涂层制备γ-Al2O3陶瓷改性载体,并利用γ-Al2O3改性的陶瓷载体制备银含量分别为25%、50%和75%的Pd-Ag二元合金膜催化剂以及Pd-Ag-Pt、Pd-Ag-Au三元合金膜催化剂,通过SEM、XRD、SEM-EDS、BET等表征手段对改性载体和合金膜催化剂进行表征,在膜反应器中进行氢氧直接合成过氧化氢反应,考察了催化剂载体改性和合金膜改性对氢氧直接合成反应的影响规律。
2.
To take approaches for nitrate pollution of groundwater effectively,the main removal approaches are compared in this paper,and catalytic reduction of nitrate in water over Pd-Cu/α-Al_2O_3 ceramic membrane catalyst is studied emphatically.
为了有效地治理地下水中硝酸盐的污染,本文在对几种主要技术进行比较的基础上,着重对Pd-Cu/α-Al_2O_3陶瓷膜催化剂催化还原水中硝酸盐进行了研究。
补充资料：膜催化
分子式：
分子量：
CAS号：
性质：将催化性能与膜的选择透过性能相结合的催化。利用膜催化可使反应产物之一离开反应体系，从而使反应进行得更加完全，避免或减轻副反应的发生，由此而提高选择性和目的产物收率。可在膜的两面进行不同热效应的反应，各自促进放热和吸热反应。还可在膜的两面分别进行如加氢和脱氢类反应。膜催化开辟了连续制备香料和其他高纯物质的新途径。可以避免贵金属催化剂的损失，简化流程和减少废料。催化剂可采用钯合金金属箔、薄壁管、沸石分子先进筛膜，载有催化活性物质的其他物料的膜。参与重要代谢过程的各种酶，也都可看做膜催化剂。
分子量：
CAS号：
性质：将催化性能与膜的选择透过性能相结合的催化。利用膜催化可使反应产物之一离开反应体系，从而使反应进行得更加完全，避免或减轻副反应的发生，由此而提高选择性和目的产物收率。可在膜的两面进行不同热效应的反应，各自促进放热和吸热反应。还可在膜的两面分别进行如加氢和脱氢类反应。膜催化开辟了连续制备香料和其他高纯物质的新途径。可以避免贵金属催化剂的损失，简化流程和减少废料。催化剂可采用钯合金金属箔、薄壁管、沸石分子先进筛膜，载有催化活性物质的其他物料的膜。参与重要代谢过程的各种酶，也都可看做膜催化剂。