1) semicontinuous emulsion copolymerization
半连续乳液共聚
1.
In the paper, a kind of size is made from such monmers as VAc, MA, MMA and AA by semicontinuous emulsion copolymerization.
采用半连续乳液共聚的方法合成了醋酸乙烯酯共聚浆料，对两种不同增稠工艺的浆料与甲酯浆作了性能对比，发现后增稠浆料的流动性最好，对涤／棉的粘结力最大，水溶时间大大缩短；所合成的浆料具有较高的玻璃化温度，热粘性能稳定，上浆效果良好，对涤／棉具有较好的增强保伸作用。
2) semi-continuous emulsion polymerization
半连续乳液聚合
1.
With this macromonomer as surfactant, we adopted methyl methacrylate, butyl acrylate, β-hyroxyethyl acrylate, methacrylic acid and crosslinking monomer to synthesize acrylic/polyurethane hybrid system through the semi-continuous emulsion polymerization process.
用该水性聚氨酯大单体为表面活性剂,用甲基丙烯酸甲酯(MMA)、丙烯酸丁酯(BA)、丙烯酸-β-羟乙酯(HEA)、甲基丙烯酸(MAA)和交联单体等单体,以半连续乳液聚合工艺合成了核壳结构水性丙烯酸-聚氨酯杂化体。
2.
The effect of the mass ratio of methyl methacrylate(MMA) to butyl acrylate(BA),namely F,on the nucleation mechanism and the particle size distribution in semi-continuous emulsion polymerization was investigated,with MMA and BA as the monomers,potassium persulfate(KPS) as the initiator and sodium dodecyl benzene sulfonate(DBS) as the emulsifier.
以甲基丙烯酸甲酯(MMA)和丙烯酸丁酯(BA)为反应单体、过硫酸钾(KPS)为引发剂、十二烷基苯磺酸钠(DBS)为乳化剂,研究了半连续乳液聚合中单体配比F(MMA/BA的质量比)对体系成核机理和粒径分布的影响。
3.
Nano emulsion is prepared by semi-continuous emulsion polymerization process with styrene and butyl acrylate as hard monomer and soft monomer respectively.
探讨了苯乙烯和丙烯酸丁酯分别作为硬单体和软单体,用半连续乳液聚合工艺制备纳米苯丙乳液的条件;研究了乳化剂类型、配比、用量和乳液固体含量对乳液聚合及乳液涂膜性能的影响,特别是在不同条件下对制得的乳液粒径、黏度、凝聚率、贮存稳定性、钙离子稳定性、涂膜外观、吸水率、光泽度等的影响。
3) Semi-continuous seed emulsion polymerization
半连续种子乳液聚合
1.
The synthesis and characterization of a novel core-shell structure and water-borne fluorinated acrylic polymer was carried out in this paper by the semi-continuous seed emulsion polymerization.
采用半连续种子乳液聚合方法,在十二烷基硫酸钠(SDS)/辛基苯基聚氧乙烯醚(OP-10)复合乳化剂的作用下,合成了以甲基丙烯酸甲酯(MM A)、丙烯酸丁酯(BA)和甲基丙烯酸十二氟庚酯(A ctyflon-G 04)为原料的水性核壳型结构的含氟丙烯酸酯聚合物乳液。
4) semi-continuous seeded emulsion polymerization
半连续种子乳液聚合
1.
2%) was prepared by semi-continuous seeded emulsion polymerization.
采用半连续种子乳液聚合法,使用丙烯酸(AA)功能性单体和丙烯酸丁酯(BA)软单体对醋酸乙烯酯(VAc)进行了共聚改性,制备出高固含量(50。
5) semi continuous seed emulsion polymerization
半连续种子乳液聚合
1.
A styrene/acrylic emulsion with a core/shell structure has been prepared from styrene,acrylic acid,butyl acrylate and other monomers by use of pre emulsifying technology and semi continuous seed emulsion polymerization method.
以苯乙烯、丙烯酸丁酯、丙烯酸等为单体 ,采用预乳化工艺和半连续种子乳液聚合方法合成了具有核 /壳结构的苯丙乳液 ,通过正交试验和综合评分的方法 ,对制备多元素丙乳液体系的影响进行较系统的研究 ,确定了制备苯丙乳液的最佳工艺参数 。
2.
A styrene/acrylic emulsion with core/shell structure by use of pre emulsion and semi continuous seed emulsion polymerization technology has been prepared The influence of initiators, emulsifier levels and ratio of amount of emulsifier in two steps on the preparation of the styrene/acrylic emulsion was discusse
采用预乳化工艺和半连续种子乳液聚合技术合成了具有核／壳结构的苯丙乳液，研究了引发剂种类、乳化剂用量及两阶段乳化剂用量比等对苯丙核／壳乳液合成的影响。
6) semicontinuous seed emulsion polymerization
半连续乳液种子聚合
1.
The butyl acrylate(BA)/styrene(ST)/methyl acrylate( MA)/methyl methacrylate(MMA)/acrylate acid (AA)/acrylamide( AM) composite emulsion was synthesized by semicontinuous seed emulsion polymerization.
采用半连续乳液种子聚合法合成了丙烯酸丁酯(BA)/苯乙烯(ST)/丙烯酸甲酯(MA)/甲基丙烯酸甲酯(MMA)/丙烯酸(AA)/丙烯酰胺(AM)复合乳液,根据正交试验结果,得出复合乳液的最佳配方。
补充资料：苯乙烯、丙烯酸共聚乳液
CAS：25085-34-1
分子式：(C8H8·C3H4O2)x
中文名称：苯乙烯、丙烯酸共聚乳液
苯丙乳液
苯丙建筑罩光液
英文名称：Styrene-acrylic latex
Acrylic acid-styrene copolymer
2-Propenoic acid, polymer with ethenylbenzene
分子式：(C8H8·C3H4O2)x
中文名称：苯乙烯、丙烯酸共聚乳液
苯丙乳液
苯丙建筑罩光液
英文名称：Styrene-acrylic latex
Acrylic acid-styrene copolymer
2-Propenoic acid, polymer with ethenylbenzene
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条