1) polyacrylatepolyurethane microemulsion film
聚丙烯酸酯-聚氨酯微乳液膜
2) polyurethane-acrylate emulsion
聚氨酯丙烯酸酯乳液
1.
The UV-curable waterborne polyurethane-acrylate emulsion modified by epoxy resin was prepared with toluenediisocyanate(TDI-80) ,polyether(N220) ,dimethylolpropionic acid(DMPA) ,1,4-butanediol(BDO) ,epoxy resin and hydroxypropyl acrylate(HPA) as the main materials.
结果表明,通过加入适量的环氧树脂,聚氨酯丙烯酸酯乳液的稳定性和耐水性得到明显改善,当二羟甲基丙酸用量为6%左右、环氧树脂用量为4%～8%、中和度为90%～95%时,所得到的聚氨酯丙烯酸酯聚合物乳液的外观和稳定性较好。
3) nanosize acrylic microlatexes
纳米聚丙烯酸酯微乳液
1.
Surface modification of nanometer CaCO_3 by nanosize acrylic microlatexes
纳米聚丙烯酸酯微乳液改性纳米CaCO_3研究
4) polyacrylate microemulsion
聚丙烯酸酯微乳液
1.
Study of factors that affect average particle size of polyacrylate microemulsion
聚丙烯酸酯微乳液平均粒径影响因素的研究
5) polyurethane-polyacrylate latex
聚氨酯-聚丙烯酸酯胶乳
6) polyacrylate emulsion
聚丙烯酸酯乳液
1.
Application of ANN in property prediction of polyacrylate emulsion;
ANN在聚丙烯酸酯乳液性质预测中的应用
2.
Factors of Affecting Polyacrylate Emulsion Adhesive Properties;
影响聚丙烯酸酯乳液胶粘剂性能的因素
3.
Study on synthesis of polyacrylate emulsion modified by silica sol via in-situ polymerization
硅溶胶原位改性聚丙烯酸酯乳液的研究
补充资料：聚丙烯酸酯乳液
分子式：
CAS号：
性质： 是指丙烯酸酯、甲基丙烯酸酯，有时再加少量的丙烯酸或甲基丙烯酸经共聚制成的乳液。该乳液对颜料的黏结能力大，耐水、耐碱、耐光、耐候等性能均较好，施工性能良好。主要用来制作外用乳胶漆，由于可用塑性不同的单体共聚，因此不必外加增塑剂。聚丙烯酸酯的弹性、延伸性能好，特别适合于涂装温度变化剧烈的物面和膨胀系数相差很大的场合。
CAS号：
性质： 是指丙烯酸酯、甲基丙烯酸酯，有时再加少量的丙烯酸或甲基丙烯酸经共聚制成的乳液。该乳液对颜料的黏结能力大，耐水、耐碱、耐光、耐候等性能均较好，施工性能良好。主要用来制作外用乳胶漆，由于可用塑性不同的单体共聚，因此不必外加增塑剂。聚丙烯酸酯的弹性、延伸性能好，特别适合于涂装温度变化剧烈的物面和膨胀系数相差很大的场合。