1) corrosion with salt coating
涂盐腐蚀
1.
Corrosion-resistance performance of coatings was evaluated by means of high temperature oxidation test, corrosion with salt coating test and thermal shock test.
应用扫描电子显微镜(SEM)、能谱仪(EDS)、X射线衍射仪(XRD)等测试手段对涂层的显微组织和常规性能进行分析,采用热震试验、高温氧化试验及涂盐腐蚀腐蚀试验方法评价涂层的耐蚀性能,并对涂层的腐蚀机理进行了研究。
2) Salt spray corrosion
盐雾腐蚀
1.
Study on salt spray corrosion of the paint coating containing flaky Zn-15Al-5Mg-Ce alloy
鳞片状Zn-15Al-5Mg-Ce合金油漆涂层的盐雾腐蚀研究
2.
The influence of salt spray corrosion on high-temperature cyclic oxidation behavior of thermal barrier coatings(TBCs) prepared by electron beam physical vapor deposition(EB-PVD) have been investigated.
研究了常温盐雾腐蚀对其循环氧化行为的影响。
4) salt spray test
盐雾腐蚀
1.
The results show that the resisting salt spray corrosion time of the microwires is above 240 h in neutral salt spray test;the average breakdown voltages of the microwires with 25 μm in outer diameter and 3.
结果表明:玻璃包覆纯铜微丝在中性盐雾实验条件下,抗潮热盐雾腐蚀时间在240 h以上;对于外径25μm、包覆层厚度3。
2.
The salt spray test of ZM5 and ZM6 which were made of different purity magnesium ingot indicated that the corrosion rate in salt spray test of ZM5 and ZM6 which were made of high purity magnesium ingot is far lower than that of low purity magnesium; the influence of magnesium ingot purity to ZM5 is more notable than that to ZM6.
对不同纯度镁锭生产的ZM5和ZM6铸造镁合金的耐盐雾腐蚀的研究结果表明,高纯镁锭能明显降低ZM5,ZM6铸造镁合金的腐蚀速率,提高合金的耐盐雾腐蚀性能。
3.
The influence of pre-corrosion on the fatigue life of ultra-high strength steel AF1410 was studied using the salt spray test and fatigue test combination method.
采用盐雾腐蚀试验与疲劳试验相结合的方法,研究了预腐蚀对AF1410超高强度钢疲劳寿命的影响,并用扫描电子显微镜分析了疲劳断口形貌特征。
5) hot salt corrosion
热盐腐蚀
6) Replies Salt Decay
复盐腐蚀
补充资料：铂改性铝涂层IN738LC耐蚀高温合金热腐蚀产物