1) sulphoaluminate cement clinker containing barium
含钡硫铝酸盐水泥熟料
1.
Sintering sulphoaluminate cement clinker containing barium from low-grade barytes and studying on its properties;
利用低品位重晶石烧制含钡硫铝酸盐水泥熟料及其性能研究
2) barium containing sulphoaluminate cement
含钡硫铝酸盐水泥
1.
The minerals of the barium containing sulphoaluminate cement are mainly 3CA· Ba-SO4, β-C_2S and a small amount of celite.
含钡硫铝酸盐水泥的主要矿物组成为含钡硫铝酸钙(简写3CA·BaSO_4)、硅酸二钙(β-C_2S)以及少量的铁相。
3) sulphoaluminate cement clinker
硫铝酸盐水泥熟料
1.
Study on performance of silicates-base cement system blending sulphoaluminate cement clinker;
掺硫铝酸盐水泥熟料的富硅酸盐水泥体系的性能研究
2.
The microstructures of two types of bauxite as well as two types of sulphoaluminate cement clinker burned by two bauxite contents were studied by using Scanning Electron Microscope.
利用扫描电子显微镜 (SEM)研究了两种铝矾土和用两种铝矾土配料煅烧的硫铝酸盐水泥熟料的微观结构形态 ,探索了铝矾土的的微观结构对硫铝酸盐水泥熟料质量的影响 ,指出了铝矾土结构密实、硬度大造成生料易磨性差 ,是最终导致硫铝酸盐水泥快凝的主要原因。
4) Ba-containing sulphoaluminate cement concrete
含钡硫铝酸盐水泥混凝土
5) Ba-bearing aluminoferriate cement
含钡铁铝酸盐水泥
1.
The effect of gypsum content on the hydration,compressive strength and setting time of Ba-bearing aluminoferriate cement was presented.
介绍了石膏含量对含钡铁铝酸盐水泥的水化、抗压强度和凝结时间等性能的影响。
6) Ba bearing sulphoaluminate
含钡硫铝酸盐
补充资料：硫铝酸盐水泥
分子式：
CAS号：
性质：用低品位的矾土和石膏、石灰按适当比例混合磨细后，在1300℃±50℃的回转窑中制得以无水硫铝酸钙(3CaO3Al2O3·CaSO4)和β-2CaO·SiO，占18％～30％为主要矿物的熟料，按与硫铝酸盐的不同摩尔比M加入石膏，可得不同性质的硫铝酸盐水泥。当M=0～1时，为快硬早强水泥，可用于抢修工程；当M=1～2时，可制得微膨胀水泥，用于锚固和刚性防水工程；M>2时，可制成自应力水泥，用于制管工程。
CAS号：
性质：用低品位的矾土和石膏、石灰按适当比例混合磨细后，在1300℃±50℃的回转窑中制得以无水硫铝酸钙(3CaO3Al2O3·CaSO4)和β-2CaO·SiO，占18％～30％为主要矿物的熟料，按与硫铝酸盐的不同摩尔比M加入石膏，可得不同性质的硫铝酸盐水泥。当M=0～1时，为快硬早强水泥，可用于抢修工程；当M=1～2时，可制得微膨胀水泥，用于锚固和刚性防水工程；M>2时，可制成自应力水泥，用于制管工程。