1) Epoxied phenolic resin
环氧化酚醛树脂
2) Phenolic epoxy resin
酚醛环氧树脂
1.
Preparation of water-borne phenolic epoxy resin latex;
水性酚醛环氧树脂乳液的制备
2.
Preparation of phenolic epoxy resin high-temperature resistance adhesives modified with silicone;
有机硅改性酚醛环氧树脂耐高温胶粘剂的研制
3.
In this essay,the chain transfer agent RAFT made in our laboratory has a reaction with phenolic epoxy resin.
本文采用本实验室制备的一种RAFT链转移剂,先与酚醛环氧树脂进行加成反应,然后通过控制丙烯酸的量再对加成后树脂进行改性,制备出了水溶性酚醛树脂;采用FTIR、GPC、DSC等测试手段对树脂的结构进行了表征,并对其性能进行了研究。
3) novolac epoxy
酚醛型环氧树脂
1.
Study on curing kinetics of novolac epoxy/bisphenol A cyanate resin system;
酚醛型环氧树脂/双酚A型氰酸酯树脂体系固化动力学的研究
4) Novolac Epoxy Resin
酚醛环氧树脂
1.
Allyl group was grafted into novolac epoxy resin,in order to take on photosensitivity.
通过在酚醛环氧树脂中引入烯丙基,以实现树脂的感光性,考察了四种催化剂和其不同用量及两种阻聚剂对反应的影响,利用配比不同的丙烯酸和酚醛环氧树脂合成出的感光预聚物,研究了其对感光组合物性能的影响。
2.
Two kinds of cyanate - epoxy resin blends, bisphenol A dicyanate - bisphenol A diglycidyl ether epoxy resin blends and bisphenol A dicyanate - novolac epoxy resin blends were prepared via melt blending process.
通过熔融共混制备了双酚A二氰酸酯/双酚A二缩水甘油醚环氧树脂、双酚A二氰酸酯/酚醛环氧树脂两种共混物。
3.
By mixing epoxy resin E-51 and novolac epoxy resin F-51 with weight ratio 1:1 the mix resin was compounded.
环氧树脂E-51和酚醛环氧树脂F-51以质量比1:1配制成混合树脂,以占环氧树脂15%的CTBN为增韧改性剂,制成预聚物,再与改性芳香胺固化剂、邻甲酚缩水甘油醚、耐高温填料等配合,配制成HT-737耐高温胶粘剂,满足了某军用飞机天线中聚苯硫醚与镀银黄铜板的粘接密封。
5) epoxy-phenolic resin
酚醛环氧树脂
1.
A special waterborne photosensitive epoxy-phenolic resin was synthesized by modification of F-44 epoxyphenolic resin with acrylic acid and succinic anhydride.
用丙烯酸和琥珀酸酐对F-44酚醛环氧树脂进行改性,合成了一种水性光敏酚醛环氧树脂。
2.
A water soluble photosensitive epoxy-phenolic resin was synthesized by modifying acrylic F-44 epoxy-phenolic resin with succinic anhydride.
用琥珀酸酐对丙烯酸改性的F-44酚醛环氧树脂作进一步的改性,合成了一种具有光敏性的水性酚醛环氧树脂,研究了催化剂种类、反应温度及反应时间对琥珀酸酐转化率的影响,并考察了原料配比对改性树脂水溶性、力学性能和耐腐蚀性能的影响。
6) epoxy phenolics
环氧酚醛树脂
1.
A phosphate flame retardant containing halogen(tris-2-chloroethyl phosphate) and inorganic flame retardant(aluminum hydroxide) were introduced into neat epoxy phenolics and paper-sludge/ epoxy-phenolic composite in order to improve their flame retardancy.
将含各类阻燃剂加入到环氧酚醛树脂和纸泥/环氧酚醛聚合物中,用UL-94等级燃烧测试法测定体系的燃烧等级,结果表明:TCEP和无机阻燃剂对环氧酚醛树脂有阻燃作用,但卤化和磷酸化的阻燃剂能增强纸浆/环氧酚醛复合材料的阻燃性。
2.
A phosphate flame retardant containing halogen(tris-2-chloroethyl phosphate) and inorganic flame retardant(aluminum hydroxide) were introduced into neat epoxy phenolics and paper-sludge/epoxy-phenolic composite in order to improve their flame retardancy.
用热塑性环氧酚醛树脂与纸泥制备纸泥/环氧酚醛复合材料,将含卤素的阻燃剂三-2-氯乙基膦酸盐和无机阻燃剂(如氢氧化铝)加入到环氧酚醛树脂和纸泥/环氧酚醛聚合物中,用UL-94等级燃烧测试法测定体系的燃烧等级;用热重分析仪和差示扫描量热仪对复合材料进行热分析,研究两体系的阻燃性。
补充资料：环氧酚醛树脂复合材料
分子式：
CAS号：
性质：以环氧酚醛树脂为基体的复合材料。环氧酚醛树脂是低分子量线性酚醛树脂在碱性催化剂作用下与过量的环氧丙烷反应制得的一种多环的氧化酚醛树脂。其特点是环氧基含量高,固化后树脂交联密度大。可采用一般环氧树脂固化剂进行固化,如叔胺、酸酐及咪唑类等。这类复合材料的耐热性介于环氧树脂和酚醛树脂复合材料之间,成型工艺性较酚醛树脂好,收缩率亦较低。缺点是树脂脆性较大,可与其他环氧树脂或增韧剂混用,以改善其工艺性及性能,这类复合材料主要作为耐热结构材料应用于航空、航天及一些民用工业中。
CAS号：
性质：以环氧酚醛树脂为基体的复合材料。环氧酚醛树脂是低分子量线性酚醛树脂在碱性催化剂作用下与过量的环氧丙烷反应制得的一种多环的氧化酚醛树脂。其特点是环氧基含量高,固化后树脂交联密度大。可采用一般环氧树脂固化剂进行固化,如叔胺、酸酐及咪唑类等。这类复合材料的耐热性介于环氧树脂和酚醛树脂复合材料之间,成型工艺性较酚醛树脂好,收缩率亦较低。缺点是树脂脆性较大,可与其他环氧树脂或增韧剂混用,以改善其工艺性及性能,这类复合材料主要作为耐热结构材料应用于航空、航天及一些民用工业中。