1) surface cross linking
表层交联
2) surface crosslinking
表面交联
1.
The research applied CaCl2 solution as surface crosslinking agent to Montmorillonite/Polyacrylate superabsorbent composite, and discussed effect of concentration of CaCl2 solution and surface cross-linking time on composite performances.
采用水溶液聚合法制备了蒙脱石/聚丙烯酸(钠)吸水保水复合材料,并用CaCl2溶液对其进行表面交联处理。
3) surface-crosslinked
表面交联
1.
SAP1 was subsequently surface-crosslinked by a mixture of ethylene glycol diglycidyl ether (EGDE) and aluminium chloride (AlCl3) to obtain the final Superabsorbent polymer (SAP2).
以丙烯酸、丙烯酰胺及丙烯磺酸钠为单体,采用水溶液聚合法制得三元共聚高吸水树脂(SAP1),用 乙二醇二环氧甘油醚与氯化铝作交联剂,对SAP1进行表面交联处理得高吸水树脂SAP2。
4) Crosstables
交叉列联表
5) Surface photocrosslinking modification
表面光交联
6) poly (sodium acrylate)
表面交联反应
1.
A novel composite super-absorbent of humic acid - poly-sodium acrylate was invented by surface cross-linking reaction of lignite humic acid and poly (sodium acrylate).
以风化褐煤为原料制备了腐植酸,采用溶液聚合法合成了聚丙烯酸钠吸水性树脂,通过表面交联反应将腐植酸(HA)与聚丙烯酸钠(PSA)复合,制得一种新的表面交联型腐植酸-聚丙烯酸钠吸水性树脂(HA-PSA)。
补充资料：Tm-002硅烷交联剂
1. 化学名称
甲基三乙酰氧基硅烷
2. 物理性质
无色至浅黄色透明液体，较低温度下可转变为白色晶体。易吸湿，可溶于醋酸酐，遇水会交联，并产生醋酸。
3. 技术规格
外观 无色至浅黄色透明液体，或白色晶体
密度（r25）g/cm3 1.1750~ 1.1800g/cm3
含量（%） ≥95
折射率(n 25d) 1.4050±0.0005
沸点（℃） 110-112/17mmhg
熔点（℃） 40.5
cl-（%） ≤0.1
4. 用途
本品主要用作室温硫化硅橡胶的交联剂。
5. 包装与储运
塑料桶包装，每桶净重10kg、25kg、100kg、180kg。密封储存于阴凉、干燥通风处，防潮防水，远离火种、热源。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。