1) near-eutectic alloy
近共晶合金
1.
A γ/NiMo near-eutectic alloy mainly consisting of NiMo intermetallic compound and Ni-based solid solution γ was fabricated by laser melting deposition process using Ni-Mo elemental powder blends.
以Ni-Mo合金粉末为原料,利用激光熔化沉积技术制备出主要由高硬度NiMo金属间化合物和高强韧性镍基固溶体γ组成的γ/NiMo近共晶合金,分析了合金的显微组织并在室温干滑动磨损条件下测试了合金的耐磨性。
2) eutectic alloy
共晶合金
1.
Investigation of formation technology of superplastic Zn-Al eutectic alloy;
超塑性锌铝共晶合金成形工艺的研究
2.
The microstructures in rotating magnetic fields have been studied for Pb-48%Sn and Pb-67%Sn hypereutectic alloys, and compared with Pb-48%Sn-0.
研究了旋转磁场对Pb-48%Sn亚共晶合金和Pb-67%Sn过共晶合金凝固组织影响的作用机理,对比分析在常规条件下和旋转磁场条件下Pb-48%Sn-0。
3.
The effects of two cyclic heat treatment processes on the microstructures and compressive properties at room temperature of Ti-Si eutectic alloy were studied.
研究了两种循环热处理工艺对钛硅共晶合金微观组织和室温压缩性能的影响。
3) eutectic alloys
共晶合金
1.
On the basis of the rapid growth model for dendrite and eutectic and the criterion of the highest temperature for interface growth, an interface response function (IRF) of eutectic alloys during rapid equiaxed solidification was established.
在快速枝晶及共晶生长理论模型基础上,使用最高界面生长温度判据,建立了共晶合金快速等轴凝固界面响应函数(IRF)模型,分析了Al-Si合金系各种相及组织的竞争生长,绘制了非平衡组织选择图。
4) hypereutectic alloy
过共晶合金
1.
7 hypereutectic alloy melt was undercooled to 407 K(0.
7过共晶合金获得了407K的大过冷度,研究了其在不同过冷度下快速凝固过程中的再辉行为。
5) eutectic Al-base alloy
共晶铝合金
6) hypoeutectic alloy
亚共晶合金
1.
6%Si hypoeutectic alloy was investigated, and the number of particles in the unit area was quantificationally surveyed by using image analysis system.
6%Si亚共晶合金非枝晶组织形成的影响,并利用图像分析仪对试样单位面积上的颗粒数进行了定量的测量。