1) needle sub-grains
针状亚晶
1.
The results show that under rapid solidification Al-45Ni-5Fe formed equiaxed grains with needle sub-grains less than 1μm, and the bend ductility can reach as high as 3.
用单辊快速凝固法制备（Ｎｉ，Ｆｅ）Ａｌ金属间化合物并研究其组织与室温塑性结果表明，Ａｌ－４５Ｎｉ－５Ｆｅ（原子分数）在快速凝固条件下可形成内部为亚微米级针状亚晶的等轴晶粒，具有高达３１％的弯曲塑性Ａｌ－３５Ｎｉ－１５Ｆｅ和Ａｌ－２５Ｎｉ－２５Ｆｅ的快凝组织则为柱状晶，弯曲塑性仅有１。
2) needle-like crystals
针状晶
1.
By using nano-titania and AlCl_3·6H_2O as raw materials,rutile TiO_2 needle-like crystals which are 25 μm in diameter and 3080 μm in length were prepared at 1 200 ℃ in NaCl and KCl fluxs.
6H2O为原料,利用NaCl和KCl复合熔盐体系在1 200℃下制备出了直径为2~5μm,长度为30~80μm的金红石型TiO2针状晶。
5) Bi_4Ti_3O_(12) platelets
TiO_2针状晶
6) whiskers
[英]['wɪskə(r)] [美]['wɪskɚ]
针状单晶
补充资料：铝合金的羽毛状晶
铝合金的羽毛状晶
feathey crystal of aluminium alloy
IUheJ旧deyumooZhuangJ旧g铝合金的羽毛状晶(feathey Crystal of alu-minium anoy)铝合金铸锭中柱状晶的变种，形状类似羽毛的晶粒。是铸锭缺陷的一种。形状近似直线状花边的羽毛状晶亦称为“花边状组织”。羽毛状晶成群出现，每群中羽毛状晶之间近似平行。羽毛状晶是双晶，以(111)晶面为双晶面。铝一镁系合金中的羽毛状晶如图所示。’ 产生羽毛状晶的工艺因素主要是:(1)熔体处于高温平稳状态，有较好的定向结晶条件。(2)在铸造温度下熔体停留时间过长，熔体过热和高度净化，减少结晶前沿形成晶核的数量。(3)合金中加入某些容易产生羽毛状晶的微量元素，如硼和错。 超硬铝合金、工业纯铝和高镁铝合金形成羽毛状晶的几率较大，而高强锻造铝合金2A70(LD7)、防锈铝合金 3A21(LF21)和含镁低于5%的铝镁系合金，基本上不形成羽毛状晶。 铸锭中存在羽毛状晶对其性能影响较大。在塑性加工过程中易在羽毛状晶的双晶面处产生裂纹。制品中残留的未完全破碎的羽毛状晶区会扩大使用性能的各向异性。蘸: 铝一镁系合金铸锭中的羽毛状晶偏光只100 (格长清)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条