1) cold-pressed briquette
冷压型煤
1.
The characteristics of dilatation and contraction of the cold-pressed briquette made of Hebi coal during carbonization was studied with a shrinkage indicator in this paper.
用型块收缩仪研究了由鹤壁煤制取的冷压型煤在炭化过程中的膨胀与收缩特性。
2) IChPW process
波兰煤化学加工研究所冷压型焦工艺
3) cold state briquetting
冷压成型
1.
Based on this analysis, a hot state briquetting process and/or cold state briquetting combination high temperature carbonization process is put f.
评述了中国工业型煤的开发和应用现状,并指出型煤质量是影响型煤市场的关键;探讨了冷压成型工艺只是使煤颗粒以物理形式的表面粘合,而热压成型工艺却是赋于煤颗粒以分子结构变化的化学形式的内在焦结,能起到质的变化;提出了热压成型工艺或"冷压成型加高温碳化"工艺,将有助于提高型煤质量和开拓型煤市场。
4) cold pressing type
冷压型
5) cold briquetting
冷压成型
1.
By using low-level Jinzhushan white coal as material and a way of cold briquetting,the preparation process of briquette used as the fuel in the limestone upright furnace is investigated.
实验以低阶金竹山白煤为原料,采用冷压成型工艺,研究了石灰竖炉用型煤的制备,分析了各成型因素对型煤质量的影响。
2.
Effects of the caking property of coal for briquetting on the cold briquetting process and the briquette carbonization process were analyzed.
分析了成型用煤粘结性对冷压成型和型煤炭化工艺的作用 ,讨论了主体煤粘结性和配粘结用煤对型煤和型焦的强度及热性质的影响。
6) cold briqueeting coke
冷压型焦
1.
For improving the quality of cold briqueeting coke, the thermal properties of cold briqueeting coke made mainly from meager-lean coal and its some influencing factors were studied.
从提高冷压型焦质量出发，对以贫瘦煤为基础煤的冷压型焦的热性质和影响热性质的某些因素进行了研究，并提出改进高炉用型焦质量的具体措施。
补充资料：焊接:冷压焊
在常温下只靠外加压力使金属產生强烈塑性变形而形成接头的焊接方法。加压变形时﹐工件接触面的氧化膜被破坏并被挤出﹐能净化焊接接头。所加压力一般要高於材料的屈服强度﹐以產生60～90％的变形量。加压方式可以缓慢挤压﹑滚压或加衝击力﹐也可以分几次加压达到所需的变形量。冷压焊的工件一般是塑性金属﹐如铝﹑铜﹑鎘﹑镍和银等。冷压焊有搭接点焊和对接焊两种。搭接点焊前工件表面须经机械加工﹐或用钢丝刷(轮)或溶剂仔细清理﹐对接焊时表面清理要求不太严格。冷压焊设备只需一台挤压机﹐包括压膜和夹持钳口﹐也可用手动夹具焊接小工件。冷压焊时工件不必加热﹐因而适於焊接不允许有温昇的工件和加热时会引起软化的材料﹐也适用於易產生脆性化合物的异种金属连接。冷压焊已应用於电容器外壳的封装﹑电气工业中铝铜过渡接头﹑导电母线﹑引出线﹑铝製日用品和包装带的焊接等。铝与铝对接可焊截面达1500毫米2 ﹐铝与铜对接可焊截面达1000毫米2 。冷压焊所需设备简单﹐工艺简便﹐劳动条件好。但冷压焊所需挤压力较大﹐在大截面工件的焊接时设备较庞大﹐搭接焊后工件表面有较深的压坑﹐因而在一定程度上限制了它的应用范围。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。