1) PVA gel filament
PVA冻胶丝
2) gel spinning
冻胶纺丝
1.
The polyvinyl alcohol (PVA) fiber water-soluble at 5 - 80℃ was prepared with methyl alcohol as a solvent by gel spinning.
通过甲醇溶剂冻胶纺丝制备水溶温度为5-80℃聚乙烯醇(PVA)水溶纤维,采用X射线衍射、双折射、电子强伸仪等测定了PVA水溶纤维的结晶度、取向度、应力应变曲线。
2.
The results showed that dimethyl sulphoxide and formamide were not rational choices for gel spinning process of high-relative viscosity nylon 6 when m- cresol, sulfonic acid and form.
结果表明:二甲基亚砜和甲酰胺不宜作高相对粘度尼龙6的冻胶纺丝溶剂,硫酸、甲酸和间甲酚比较适宜;提高温度有利于降低剪切速率,质量分数为12％的间甲酚溶液和质量分数为9％的甲酸溶液作溶剂,其尼龙6溶液分别在50～60℃和45℃以上有较好的可纺性;溶剂对尼龙6晶体结构的形成有着重要的影响。
3.
The ultrahigh molecular weight polyethylene/carbon nanotube (UHMWPE/CNTs) composite fiber was prepared by gel spinning process.
利用冻胶纺丝的方法制备了超高相对分子质量聚乙烯／碳纳米管(UHMWPE／CNTs)复合纤维,以高锰酸钾和硫酸为氧化剂对CNTs进行纯化处理,用DNZ-201钛酸酯对纯化处理后的CNTs进行功能化处理。
3) gel-spinning
冻胶纺丝
1.
The structural characteristics and relative parameters of twin screw extruder used in gel-spinning have been analysed and discussed extensively.
对双螺杆挤出机用于冻胶纺丝，其结构特性及相关设计多数进行了详细的分析和探讨，同时提出了一些参考建议，经特殊设计加工后的双螺杆挤出机应用在冻胶纺丝工艺上，成功地纺制出高强高模聚乙烯纤维。
2.
In this paper, the domestic mineral oil is employed as solvent, UHMWPE fiber with excellent mechanical properties is prepared by dissolving, gel-spinning, extracting and ultrahigh drawing.
纺制UHMWPE纤维最为成熟且早已工业化的方法为冻胶纺丝—超拉伸法。
3.
The gel-spinning and ultra-drawing method is used in the industry.
由于其优越的性能而得到广泛应用,工业上采用冻胶纺丝一超倍热拉伸技术制得。
4) gelation-spinning
冻胶纺丝
1.
The dual copolymer resin which can absorb oil made up of butyl methacrylate,hydroethyl methacrylate was synthesized by suspension polymerization,then the fiber-like copolymer resin was prepared by gelation-spinning.
采用悬浮聚合法合成了甲基丙烯酸正丁酯、甲基丙烯酸β羟乙酯二元共聚树脂,并用冻胶纺丝技术制备了纤维状共聚物树脂。
5) gel-spun fiber
冻胶丝
1.
The effects of extraction,drying and stretching conditions and the maximum draw ratio,structure and properties of UHMWPE gel-spun fibers were discussed.
探讨了超高相对分子质量聚乙烯冻胶丝在后续拉伸过程中的萃取、干燥和拉伸条件对拉伸性能和结构性能的影响。
补充资料：胶丝
分子式：
CAS号：
性质：又称胶丝、胶带。用纯天然橡胶或天然胶乳制成，截面分为圆形(胶乳制)、方形和长方形(胶带)，系表面光滑、有弹性的线状或带状橡胶产品。用天然橡胶经压延、卷筒、硫化罐硫化后，再切成线(方截面)或带(长方形截面)；或用胶乳压出成型经连续硫化制成圆形截面胶线。用于编织弹性织物，如各种松紧带、松紧鞋口和袜口等。
CAS号：
性质：又称胶丝、胶带。用纯天然橡胶或天然胶乳制成，截面分为圆形(胶乳制)、方形和长方形(胶带)，系表面光滑、有弹性的线状或带状橡胶产品。用天然橡胶经压延、卷筒、硫化罐硫化后，再切成线(方截面)或带(长方形截面)；或用胶乳压出成型经连续硫化制成圆形截面胶线。用于编织弹性织物，如各种松紧带、松紧鞋口和袜口等。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条