1) large deformation band
大变形带
1.
Maximum strain points were positioned on the large deformation bands at a distance from crack tip.
实验结果表明：在裂尖两侧存在与裂纹方向夹角约为５０°的大变形带。
2) deformation band
变形带
1.
Analysis on deformation band in rock under axisymmetrical condition based on bifurcation theory;
基于分叉理论的轴对称条件下岩石变形带分析
2.
Finite element numerical implementation for simulation of deformation band in saturated sand
饱和砂土局部变形带模拟的有限元数值实现
3) deformation band
形变带
1.
The observation results show that in the process from the formation of deformation band (DB) to the appearance of fatigued crack, the spacing between the wall structures in DB keeps constant.
采用电子通道衬度技术对垂直晶界Cu双晶在疲劳过程中位错组态的演化与裂纹的形核进行了研究,结果表明,形变带中墙结构的间距从形成之初到疲劳裂纹出现始终保持恒定;穿晶裂纹与沿晶裂纹尖端的位错组态均为胞结构;裂纹优先从形变带产生。
2.
5×10-3, two types of deformation bands (DBI and DBII)formed on the specimen surface and their habit planes are perpendicular to each other strictly.
5×10－3时，表面出现两种宏观形变带（DBI和DBII）；它们呈严格的正交关系，其形成可能与循环加载中产生的不可逆晶体旋转密切相关。
4) deformed band
形变带
1.
deformed band and transformed band, are formed in cutting process.
研究结果表明 ,切削过程中形成了两种类型的绝热剪切带即形变带和转变带 ,随着绝热剪切带的形成和发展切屑形态发生改变。
2.
e, deformed band w.
结果表明:低速下形成以组织剧烈拉长为特征的形变带,高速下形成以组织严重细化为特征的转变带;工件硬度的提高有利于形成转变带;增加切削速度和工件硬度对转变带硬度影响很小,但会显著提高形变带硬度。
3.
The results show that, after localization of shear deformation, there were two types of adiabatic shear bands, one was "deformed band" with elongated microstructure along shear zones at lower cutting speed, the other was "transformed band" with fine grains at higher cutting speed.
结果表明:在剪切变形局部化发生以后,会形成两种形式的ASB,即在低速下形成的以大塑性变形为特征的形变带和高速下形成的以组织细化为特征的转变带。
6) deformation bands
变形带
1.
By employing a dynamic digital speckle pattern interferometry technology, the evolution of the three types of PLC deformation bands (type A,B,C) was observed directly in Al-Cu alloys under constant tensile strain rate.
实验记录了三种类型的PLC(Portevin LeChatelier)变形带 (类型A、B、C)在试件表面的产生过程 ;追踪了它们产生和传播的空间轨迹 ;探讨了在室温下出现不同类型PLC带所必需的加载应变率范围 (当 ε≥ 5× 1 0 - 4 s- 1 时 ,变形过程中以A类型的PLC带为主 ;当 ε <3× 1 0 - 5s- 1 时 ,则大量出现C类型的PLC变形带 ;而B类型的带将出现于这两者之间 ) ;并对”锯齿形”应力曲线中应力下掉的幅值进行了统计研究。
2.
They are mainly concerned with influences of micro-defects to the mechanical behavior of cell-structure,analyses of cell collapse,responses of cell morphology to applied loads, experimental explanations of the origin, development of deformation bands and a theoretical model of open-cell structure of the materials.
概要叙述了泡沫金属材料的制备方法 ,着重介绍了泡沫金属材料孔结构力学行为方面的研究成果 ,主要讨论了微缺陷对孔结构力学性能的影响、孔失效机理、孔的几何形态对荷载作用的敏感性、变形带的形成和发展以及开孔结构的理论力学模型 。
补充资料：变形带
变形带
deformation band
b ianxingdai变形带(deformation band)晶体均匀变形时产生的、取向不同的很薄带状区域。变形带是平行的滑移面内异号刃型位错(见滑移)交互作用使晶体发生弯折所形成的。带中的晶格相对于周围晶体中未变形部分旋转了几度或几十度。当外部应力不超过临界切应力几时，两个在平行滑移面上相向运动的异号刃型位错，将如图所示停留在彼此分开一定距离处.这些位错将阻止在其后面运动的其他位错而造成位错塞积，塞积位错将抑制在邻近面上位错的滑移并促使出现新的塞积，结果逐渐形成变形带，负刃型位错在带的一边，正刃型位错则处于另一边。 爆蜘\2 籍 变形带形成的位错示意图 a一单滑移;b一双滑移 1一变形带式弯折面;2一滑移面 晶体经过变形，通过随后的表面抛光可以使滑移线消失，但即使经过反复抛光和腐蚀后仍可观察到变形带，因为变形带代表不同晶向的区域。单晶体中能够产生几毫米宽的变形带，但在多晶体试样中需用显微镜才能见到。变形期间由于晶界的阻碍，容易在一个晶粒内引起取向的不同，故而多晶体试样形成变形带的倾向更大。变形带一般呈不规则形状，但是它是沿主变形方向延伸的。带的轮廓一般模糊而不明显，表明取向差是渐渐消失的。已经在体心及面心立方晶格的金属中观察到变形带，但在密集六方晶格金属中尚未见到。 变形带与扭拆带之间的主要差别是:在形成变形带的情况下位错运动在带外发生，带中的晶格保持原来的取向;而在形成扭折带的情况下，塑性变形和晶格的重新取向在带内发生。 (王祝堂)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。