1) oscillographic impact test
示波冲击弯曲试验
2) impact bending test
冲击弯曲试验
1.
The impact fatigue property of cemented carbide was studied by impact bending test in this paper.
采用冲击弯曲试验研究了硬质合金的冲击疲劳性能。
3) blow bending test
弯曲冲击试验
4) Instrumented impact test
示波冲击试验
1.
This paper reports the dynamic fracture toughness and impact properties of 10Cr9Mo1VNbN steel from CVN instrumented impact testing at a wide temperature range from -196 to 650 ℃.
采用标准夏比Ｖ型缺口试样的示波冲击试验获得了１０Ｃｒ９Ｍｏ１ＶＮｂＮ钢的冲击特性和动态断裂韧度，对冲击过程进行了断裂力学分析，并检验了裂纹启裂能量、裂纹扩展能量、总冲击能量、动态断裂韧度之间的相关性。
2.
By means of the instrumented impact test and the fracture morphology analytic technique,the impact fracture behavior of SiC particulates reinforced A359 composites (SiC p/A359) fabricated by melt stir casting is studied.
采用示波冲击试验及断口形貌分析技术，对液态搅拌铸造ＳｉＣｐ／Ａ３５９ 复合材料的冲击断裂行为进行了研究。
5) instrumented charpy impact
示波冲击试验
1.
By contrast with the fractographic characteristic, the P91 steel property parameters of instrumented charpy impact test has been analysed.
采用示波冲击法研究了回火温度对P91钢动力强韧性的影响,通过分析P91钢示波冲击试验性能的差异及产生原因,并结合分析各试样的断口形貌,得出最佳回火温度为750～780℃。
6) repeated transverse impact test
反复弯曲冲击试验
补充资料：机械工程材料:弯曲试验
测定材料承受弯曲载荷时的力学特性的试验﹐是材料机械性能试验的基本方法之一。弯曲试验主要用於测定脆性和低塑性材料(如铸铁﹑高碳钢﹑工具钢等)的抗弯强度并能反映塑性指标的挠度。弯曲试验还可用来检查材料的表面质量。弯曲试验在万能材料机上进行﹐有三点弯曲和四点弯曲两种加载荷方式(见图 弯曲加载方式示意图 )
。试样的截面有圆形和矩形﹐试验时的跨距一般为直径的10倍。对於脆性材料弯曲试验一般只產生少量的塑性变形即可破坏﹐而对於塑性材料则不能测出弯曲断裂强度﹐但可检验其延展性和均匀性展性和均匀性。塑性材料的弯曲试验称为冷弯试验。试验时将试样加载﹐使其弯曲到一定程度﹐观察试样表面有无裂缝。
。试样的截面有圆形和矩形﹐试验时的跨距一般为直径的10倍。对於脆性材料弯曲试验一般只產生少量的塑性变形即可破坏﹐而对於塑性材料则不能测出弯曲断裂强度﹐但可检验其延展性和均匀性展性和均匀性。塑性材料的弯曲试验称为冷弯试验。试验时将试样加载﹐使其弯曲到一定程度﹐观察试样表面有无裂缝。 说明：补充资料仅用于学习参考，请勿用于其它任何用途。