Growth of ZnO nanowires by free-catalytic thermal evaporation of ZnS powder;
无催化热蒸发ZnS粉末制备半导体ZnO纳米带
2.
Aligned cone-shaped nano-ZnO structure has been synthesized by thermal evaporation of mixtures of Zn powder,C powder and ZnO powder through one step,which overcomes the disadvantage of the previous methods through two steps: preparation catalyst first and then synthesis of nano-ZnO.
将锌粉、炭粉和氧化锌粉末混合,用简单的热蒸发方法一步就合成了大量的尖锥状纳米ZnO阵列,该方法克服了其它制备方法需要先单独制备催化剂再合成ZnO的缺点而且得到产物不含杂质。
3.
Tin oxide nanoshuttle arrays were synthesized by thermal evaporation.
利用热蒸发法在硅衬底上合成了二氧化锡纳米梭阵列,并研究其场致电子发射特性。
4) thermal evaporation
热蒸发法
1.
Synthesis of ZnMgO Nanomaterials by Thermal Evaporation and Properties Characterization;
热蒸发法制备ZnMgO纳米材料及其性能表征
2.
Diamond-like carbon nanowires were synthesized by a thermal evaporation method.
采用热蒸发法制备了类金刚石碳纳米线,利用透射电子显微镜(TEM)和高分辨率透射电子显微镜(HRTEM)对样品的形貌和结构进行观察,发现该碳纳米线具有圆形实心结构,表面光滑,直径1040nm;拉曼光谱研究显示特征峰出现在1352cm-1和1586cm-1处,为典型的类金刚石结构。
3.
This paper reviews the progresses in preparation of ZnO hollow micro/nano spheres by use of simple thermal evaporation method.
文中详细地综述了由相对简单的热蒸发法合成ZnO微纳米空心球结构的制备情况和研究进展,主要包括用热蒸发法制备ZnO微纳米空心球的生产设备与过程、实验条件、产品形貌和生长机理几个方面。
5) Electrothermal vaporization
电热蒸发
1.
A method has been developed to determining directly and simultaneously the trace elements (Ca?Fe?Mn?Cu and Zn) in the food sample (maize powder) by electrothermal vaporization inductively coupled plasma atomic emission spectrometry (ETV-ICP-AES) using slurry sampling.
建立了悬浮体制样电热蒸发电感耦合等离子体原子发射光谱 (ETV -ICP -AES)法直接同时测定食品中微量元素的方法。
2.
A method was described of directly determing trace elements (La, Yb, Y Cu and Cr) in tea by electrothermal vaporization inductively coupled plasma atomic emission spectrometry (ETV-ICP-AES) using polytetrofluoroethylene (PTFE) as chemical modifier.
以聚四氟乙烯悬浮体为氟化剂 ,对悬浮体制样电热蒸发电感耦合等离子体原子发射光谱法 (ETV -ICP -AES)直接测定茶叶中的痕量元素La、Yb、Y、Cu、Cr的蒸发行为及主要影响因素进行了研究。
3.
The recent development of electrothermal vaporization/ICPAES and its application in the analysis of rare earth elements was reviewed in this paper.
评述了电热蒸发电感耦合等离子体原子发射光谱分析 (ETV -ICP -AES)联用技术的新近进展及其在痕量稀土元素检测中的应用。
6) Thermoevaporate Hydrocarbon
热蒸发烃
补充资料：DDS蒸发热力系统
丹麦DDS公司所属糖厂能源消耗居世界最低水平，其节能经验概括起来是：采用五效蒸发和先进的热力系统；充分利用通常未利用的低温热源；采用热能压缩技术；尽可能抽用后效汁汽；千方百计节约生产工艺过程用汽等。 我国甜菜糖厂大多采用三效压力蒸发带浓缩罐，或四效真空蒸发； DDS公司所属五家糖厂中，除附有精练糖加工的萨克斯科宾糖厂外，其余四家糖厂全都采用五效蒸发（见附图）；其优点不仅蒸汽利用系数高，而且为抽用更后效的汁汽创造了条件。 DDS糖厂五效蒸发的温度条件见附表： 五效蒸发温度条件 蒸发罐效数 一 效 二 效 三 效 四 效 五 效 糖汁温度℃ 130 124 116 102 85 加热汽鼓温度℃ 136 129.3 122.8 113.3 98.3 采用这种温度条件的意图是，将三效、四效糖汁温度分别保持在116℃和 102℃(有些厂保持在104℃)，从而为充分利用三、四效汁汽煮糖创造条件。 采用五效蒸发后，一效糖汁温度必须提高；为了减少蒸发时糖汁色值增加，DDS糖厂选定了130℃；实践说明、采用这一温度，蒸发过程色值增加不多，属可以接受的范围 (但要求蒸发的汁热稳定性高)。 据DDS公司介绍，将第五效浓糖汁(糖浆)的温度设定为85℃，而不采用更低的温度，是为了有利于煮糖；此外，还因DDS糖厂可以利用五效汁汽先进行一次加热，然后才去冷凝器，所以虽然将五效糖汁温度定为85℃，也不会造成过多的热量损失。 |
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条