1) dispersive strengthening alumina
弥散增强氧化铝
1.
On dispersive strengthening alumina with nanometer-sized zirconia;
纳米氧化锆弥散增强氧化铝陶瓷的实验研究
2) ODS copper-base alloys
氧化铝弥散铜
3) ODS
氧化物弥散强化
1.
Manufacturing Process and Structure Control of ODS MGH 956 Alloy Sheet;
氧化物弥散强化MGH956合金薄板的加工工艺和组织控制
2.
In rencent years,some mechanically alloyed(MA),oxide dispersion strengthened(ODS)ferritc alloy have exhibited dramatically improved high temperature creep properties at high temperatures.
近年来,多种氧化物弥散强化(ODS)铁基高温合金表现出优良的高温力学性能尤其是高温蠕变性能,并且可以比传统铁基高温合金应用于更高的温度。
4) oxide dispersion strengthening
氧化物弥散强化
1.
The in-depth analysis of the mechanism of oxide dispersion strengthening can provide a reference for developing better quality dispersion-strengthened platinum or platinum-rhodium alloys.
运用位错理论,综述氧化物弥散强化Pt/Pt-Rh合金的机理。
5) oxide dispersion strengthened
氧化弥散强化
6) dispersion strengthened copper oxygen
弥散强化无氧铜
补充资料：氧化铝颗粒增强体
分子式：
CAS号：
性质：通常由于加入到金属基中。譬如：在Al合金中加入体积分数为30％，粒径为0.3μm的Al2O3颗粒，使材料在300℃时的拉伸强度仍达到220MPa，并且所加入氧化铝颗粒，还可促进致密化，而合金的电导率并不降低。目前，氧化铝颗粒增强铝、镁或钛合金正用于制备内燃机引擎。氧化铝颗粒也被加入到Ni-AlIC-221，制成金属间化合物基复合材料(IMCS)。氧化铝颗粒与基体具有很好的化学相容性，几乎不发生界面化学反应。这种复合材料的弹性模量比基体材料或普通Ni基合金要高出20％～30％。
CAS号：
性质：通常由于加入到金属基中。譬如：在Al合金中加入体积分数为30％，粒径为0.3μm的Al2O3颗粒，使材料在300℃时的拉伸强度仍达到220MPa，并且所加入氧化铝颗粒，还可促进致密化，而合金的电导率并不降低。目前，氧化铝颗粒增强铝、镁或钛合金正用于制备内燃机引擎。氧化铝颗粒也被加入到Ni-AlIC-221，制成金属间化合物基复合材料(IMCS)。氧化铝颗粒与基体具有很好的化学相容性，几乎不发生界面化学反应。这种复合材料的弹性模量比基体材料或普通Ni基合金要高出20％～30％。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。