1) chloride-polysulfonamide
芳香含氯聚砜酰胺
1.
The effect of the technology of thermal stretching on chloride-polysulfonamide (Cl-PSA) fiber spun by wet methods is studied in this paper.
观察芳香含氯聚砜酰胺纤维结构性能对拉伸倍率和温度的依赖性。
2) chaoried-polysulfonamide freshly formed filament
芳香合氯聚砜酰胺初生丝
3) poly(amide-sulfone)
聚芳砜酰胺
1.
A series of poly(amide-sulfone) with different intrinsic viscosity were synthesized via 4,4′-DDS,3,3′-DDS and TPC at low temperature.
以4,4′-二氨基二苯基砜(4,4-′DDS),3,3′-二氨基二苯基砜(3,3-′DDS),对苯二甲酰氯(TPC)为单体,通过低温溶液缩聚反应合成了一系列聚芳砜酰胺三元共聚物。
4) aromatic polyamide
芳香聚酰胺
1.
Preparation and influence factors of aromatic polyamide nanofiltration membrane;
芳香聚酰胺纳滤膜的制备及影响因素
2.
Preparation and Separation Performance of Aromatic Polyamide Nanofiltration Membrane;
芳香聚酰胺纳滤膜的制备及性能研究
3.
Based on the relationship between polymer structures and properties, model tri-block copolymers with a chain sequence of aliphatic polyamide-aromatic polyamide-aliphatic polyamide were designed and synthesized by the so-called "one step" and "two step" high-temperature polycon-densation.
采用高温溶液直接缩聚一步法和两步法分别合成了含全对位结构和含间位结构芳香聚酰胺预聚物及其脂肪聚酰胺-芳香聚酰胺-脂肪聚酰胺嵌段共聚物。
5) polyarylene sulfide sulfone amide
聚芳硫醚砜酰胺
1.
Diamine monomer containing sulfide was synthesized firstly,then polyarylene sulfide sulfone amide(PASSA)with high molecular weight was synthesized at low temperature.
与以往的以硫化钠为硫源采用高温聚合合成聚芳硫醚类树脂的方法不同,采用先合成含硫醚键的单体,然后进行低温溶液缩聚,合成了高分子量的新型聚芳硫醚砜酰胺(PASSA)树脂,其特性粘度可达到0。
2.
Diamine monomers containing sulfone or ketone group were synthesized firstly,then polyarylene sulfide sulfone amide(PASSA) and polyarylene sulfide ketone amide(PASKA) with high molecular weight were synthesized by a low temperature polycondensation reaction in anhydrous N-methylpyrrolidone (NMP).
采用先合成含硫醚键的单体,后进行低温溶液缩聚的方法,合成高分子量的新型聚芳硫醚酰胺类树脂——聚芳硫醚砜酰胺(PASSA)和聚芳硫醚酮酰胺(PASKA),其特性粘数分别为0。
6) aromatic polysulphonamide fiber
聚芳砜酰胺纤维
补充资料：聚砜
[—SO2—R—]n 主链上含有砜基(—SO2—)的一种热塑性树脂，若其中R为芳基，则称聚芳砜,主链中含有醚键的聚砜，又称聚醚砜。聚芳砜和聚醚砜是良好的工程塑料，具有优良力学性能、抗蠕变性、硬度和耐磨性，并具有较高的玻璃化转变温度，可在150～200℃的温度范围内长期使用。它有优良的耐化学腐蚀性，对酸、碱、盐类等都较稳定，但在酮类、酯类及齿代烃等极性溶剂的作用下易发生应力开裂。聚芳砜和聚醚砜适于模压或注射成型加工，可制作电性能优良的电子器件和印刷电路基材,还可作汽车中的特殊零部件和需耐温180℃的自动传动装置等。1965年美国联合碳化物公司首先以双酚A和4，4′- 二氯二苯砜为原料经缩聚生产聚砜。工业上生产聚砜的主要方法是使卤代芳砜与酚盐反应。常用的卤代芳砜为4，4′- 二氯二苯砜，芳酚盐为双酚A的钾盐或钠盐。这一方法反应条件较温和，生产成本较低，利于工业生产。