1) carbon whisker
碳晶须
2) carbon fibre
碳晶须
1.
The secondary reinforcement, carbon whiskers, may grow on the surface ofparent reinforcement, carbon fibres, by chemical vapour growth from acetylene using Fe saltsolution as catalyzer.
用铁做催化剂,乙炔做原料气体,在碳纤维表面上长出二级增强相——碳晶须初步考察了生长温度、铁盐溶液浓度对碳晶须生长的影响结果表明,碳晶须生长的最佳温度在1000℃左右,在催化剂溶液浓度适当时,碳晶须均匀分布在母体纤维上,并把相邻的碳纤维连结起来;温度过高或催化剂溶液浓度过高,都会在碳纤维表面上形成大块碳沉积团碳晶须的生长是气相中的碳原子溶解于纤维表面上的催化剂液滴后,在液滴底部的碳纤维表面上析出固体碳的动态过
3) porous carbon whisker
多孔碳晶须
4) coiled carbon whiskers
螺旋形碳晶须
1.
Influence of catalyst on the growth of coiled carbon whiskers;
催化剂对螺旋形碳晶须生长的影响
2.
Preparation and thermotics property of coiled carbon whiskers by CVD method;
螺旋形碳晶须的CVD法制备及热学性能
3.
The growth conditions of the coiled carbon whiskers were examined.
以Ni粉为催化剂,在高温下催化热解乙炔(C2H2),制备出了螺旋形碳晶须材料。
5) graphite whisker
高模量碳晶须
6) Al-Ti-C grain refiner
铝钛碳晶粒细化剂
1.
The new preparation method of Al-Ti-C grain refiner was studied with aluminium ingot,potassium hexafluorotitanate,aluminium powder,hexachloroethane and carbon powder.
提出了利用铝锭、氟钛酸钾、铝粉、六氯乙烷和碳粉制备铝钛碳晶粒细化剂的新方法。
补充资料：碳晶须
分子式：
CAS号：
性质：一种非金属晶须。含碳量99％以上的碳针状单晶，直径5～60μm，长度4至几十厘米，密度2g/cm3以上，强度0.7～3.4GPa，模量294～412GPa，伸长率0.2％～0.8％，耐热性好。制法是以二茂铁为催化剂、氢为载体气、苯为碳素源，在1000～1150℃的管式反应炉内进行气相成长，每分钟约4～5cm长。用作树脂基和碳基复合材料增强体。