1) minimum blank holder force
最小压边力
1.
At the same time,the formula for the minimum blank holder force has also been derived which ensures that the blank holder will not be lifted during the drawing of parts.
同时 ,又得到了保证拉深零件时压边圈不被抬起的最小压边力公
3) the minimum pressure drop
最小压力降
4) minimum back pressure
最小背压力
5) maximum edge pressure
最大边缘压力
6) minimum miscibility pressure
最小混相压力
1.
Determination of the minimum miscibility pressure of CO-2 and crude oil system by vanishing interfacial tension method;
用界面张力法测定CO_2与原油的最小混相压力
2.
Determination and prediction of minimum miscibility pressure in CO_2 flooding;
CO_2驱最小混相压力的测定与预测
3.
Determination of minimum miscibility pressure between formation crude and carbon dioxide in Fan 124 block of Daluhu oilfield.;
大芦湖油田樊124块地层油与二氧化碳最小混相压力的确定
补充资料：各种材料拉深时的单位压边力数据
在单动压力机上拉深时的单位压边力
材 料 | q/MPa |
铝 | 0.8～1.2 |
紫铜,杜拉铝(退火的或刚淬火的) | 1.2～1.8 |
黄铜 | 1.5～2.0 |
压轧青铜 | 2.0～2.5 |
20钢、08钢、镀锡钢板 | 2.5～3.0 |
软化耐热钢 | 2.8～3.5 |
高合金钢,高锰钢,不锈钢 | 3.0～4.5 |
在双动压力机上拉深时的单位压边力
工件复杂程度 | q/MPa |
难加工件 | 3.7 |
普通加工件 | 3.0 |
易加工件 | 2.5 |
材 料 | 单位压边力q/MPa |
铝(退火状态) | 0.8～1.2 |
铝(硬态) | 1.2～1.4 |
黄铜(退火状态) | 1.5～2.0 |
黄铜(硬态) | 2.4～2.6 |
铜(退火状态) | 1.2～1.8 |
铜(硬态) | 1.8～2.2 |
康铜BMn40-1.5(硬态) | 2.6～2.9 |
可伐合金4J29(退火状态) | 3.0～3.3 |
钼(退火状态) | 4.0～4.5 |
软钢t＜0.5mm | 2.5～3.0 |
软钢t＞0.5mm | 2.0～2.5 |
不锈钢1Cr18Ni9Ti | 4.5～5.5 |
镍铬合金Cr20Ni80 | 3.5～4.0 |