1) TLM(Ti-3Zr-2Sn-3Mo-15Nb) alloy
TLM(Ti-Zr-Sn-Mo-Nb)合金
2) Ti-Fe-Mo-Mn-Nb-Zr alloy
Ti-Fe-Mo-Mn-Nb-Zr合金
3) Zr-Sn-Nb alloy
Zr-Sn-Nb合金
1.
The specimens of Zr-Sn-Nb alloy with two different composition were treated in different ways as 1 000 ℃-0.
将两种Zr-Sn-Nb合金样品分别进行1000℃-0。
2.
Hot-rolling, cold-rolling and quenching tests of Zr-Sn-Nb alloy were carried out at 750℃, 780℃, 800℃ and 820℃, respectively.
对Zr-Sn-Nb合金在4种温度(750℃、780℃、800℃和820℃)下进行了热/冷加工和最终再结晶退火,并对在上述4种温度下加热的试样进行了淬火处理。
3.
The corrosion products on the I-SCC fracture of Zr-Sn-Nb alloys have been investigated by SEM and EDXA.
利用SEM和EDXA对Zr-Sn-Nb合金碘致应力腐蚀断口上的腐蚀产物进行了观察分析。
5) Ti-Nb-Zr alloy
Ti-Nb-Zr合金
6) Mo-Ti-Zr alloy
Mo-Ti-Zr合金
1.
Influence of (Mo, Zr, Ti)_xO_y particles on mechanical properties and microstructure of rotary forging Mo-Ti-Zr alloy;
(Mo,Zr,Ti)_xO_y粒子对旋锻Mo-Ti-Zr合金性能和组织的影响
补充资料：Mo-Ti-Zr-C alloy
分子式：
CAS号：
性质：由较高含量的钛、锆、碳与钼所组成的钼合金。最著名的称为TZC钼合金，含量为（%质量）钛1.25、锆0.15、碳0.15。该合金的硬度、高温强度比TZM钼合金高，但塑性较差，加工比较困难。钼钛锆碳合金可由熔炼成锭或粉末烧结成锭后加工制取各种型材，但要求较高的加工温度和加工压力。TZC钼合金主要以棒材、盘材用作金属高温热加工的模具，如粉末高温合金的等温锻造模具，有色及黑色金属的压铸模具、无缝钢管的穿孔顶头等。
CAS号：
性质：由较高含量的钛、锆、碳与钼所组成的钼合金。最著名的称为TZC钼合金，含量为（%质量）钛1.25、锆0.15、碳0.15。该合金的硬度、高温强度比TZM钼合金高，但塑性较差，加工比较困难。钼钛锆碳合金可由熔炼成锭或粉末烧结成锭后加工制取各种型材，但要求较高的加工温度和加工压力。TZC钼合金主要以棒材、盘材用作金属高温热加工的模具，如粉末高温合金的等温锻造模具，有色及黑色金属的压铸模具、无缝钢管的穿孔顶头等。