1)  compound mineral admixture
复合矿物掺合料
1.
In this experiment,the abrasion resistance of concrete mixed with expansive compound mineral admixture is studied.
试验研究了添加膨胀组分的复合矿物掺合料的混凝土耐磨性能。
2.
Based on the optimization of raw material with optimizing proportion,adopting good powder of fine grinding slag,fly ash and silica fume as compound mineral admixture with high performance water reducing agent,using small percentage of water cement ration,C90 high-strength concrete may be manufactured successfully.
本文结合河南地区地材情况,通过对原材料优选和优化配比,采用基于优质磨细矿粉、粉煤灰、硅灰的复合矿物掺合料和高效减水剂,成功配制C90级高强混凝土。
3.
In this experiment,the short-term frost resistance of concrete mixed with expansive compound mineral admixture is studied.
研究了添加膨胀组分的复合矿物掺合料混凝土的短期抗冻性能。
2)  composite mineral admixture
复合矿物掺料
3)  mineral admixtures
矿物掺合料
1.
Effects and mechanisms of mineral admixtures on sulfate attack of cement mortars;
矿物掺合料对水泥砂浆硫酸盐侵蚀的影响及机理
2.
Effect of mineral admixtures and superplasticizer on rheological performance of cement based materials;
矿物掺合料与高效减水剂对水泥基材料流变性能的影响
3.
Effective investigations of concrete additive and mineral admixtures on Sulfate attack resistance;
外加剂与矿物掺合料对混凝土抗硫酸盐侵蚀的有效性研究
4)  mineral additive
矿物掺合料
1.
The influence of mineral additive on structure light aggregate concrete strength;
矿物掺合料对结构轻集料混凝土强度的影响
2.
Study on resistance to magnesium sulfate attack on concrete containing mineral additive;
矿物掺合料对混凝土抗硫酸镁侵蚀的有效性研究
3.
On the basis of testing,this paper summarizes the influences of types of mineral additive and mixing ration on the compression strength of concrete and the penetration performance of chloride ion,and points out that adding mineral additive into concrete construction can man ameliorate performing requirements of concrete,in order to offer a reference for concrete construction.
在试验的基础上总结了矿物掺合料的种类和掺合比例对混凝土的抗压强度和氯离子渗透性能的影响,指出混凝土施工中增加矿物掺合料可以改善混凝土的性能要求,为混凝土施工提供参考借鉴。
5)  mineral additives
矿物掺合料
1.
mineral additives and water,and then they became condensates.
本文研究了以上海市管沟污泥为原料,加入一定比例的固化剂和矿物掺合料使之固结,经养护,满足路用性能,测试其固结体重金属溶出量亦满足国家标准,即污泥中的重金属离子得到有效的束缚和稳定固化,既解决了环境问题,又为污泥产业化发展开辟了新的途径。
2.
Municipal sewage sludge was mixed with solidification reagent,mineral additives and water,and then they became condensates.
研究了以上海市污水污泥为原料,加入一定比例的固化剂和矿物掺合料使之固结,经养护满足路用强度性能,测试其固结体重金属离子浸出质量浓度亦满足国家固体废弃物排放标准,即污泥中的重金属离子得到有效的束缚和稳定固化,既解决了环境问题,又为污泥产业化发展开辟了新的途径。
3.
In this experi ment,silicafume,fly ash,slag and metakaolin had beenselected as mineral additives to confect concrete by the means of adding one,two or three kinds of mineralsintothe admixture.
选用硅灰、粉煤灰、矿渣粉及偏高岭土等活性矿物掺合料,控制活性掺合料的总掺量为胶凝材料的40%等量取代水泥,采取单掺、双掺、三掺的方式配制混凝土,通过对比各组混凝土试样的力学性能、抗腐蚀性能及微观结构,探讨活性矿物掺合料的复合效应以及对混凝土性能的影响。
6)  mineral admixture
矿物掺合料
1.
Research on the ages of osmosizing performance of mineral admixture anti-chloride;
掺矿物掺合料混凝土抗氯离子渗透性龄期研究
2.
Effect of different mineral admixtures on physical characteristics of building gypsum;
不同矿物掺合料对建筑石膏物理性能的影响
3.
Investigations into the issues in the production and application of mineral admixtures;
矿物掺合料生产和应用中的若干问题
补充资料:掺合料


掺合料
admixture

  减少用水量和水泥用量,从而降低了混凝土的水泥水化热温升,对防止混凝土温度裂缝十分有利。③混凝土中砂粒之间的空隙是靠水泥浆液填充的,掺合料能替代一部分水泥浆液的体积,减少混凝土的用水量,使混凝土的密实性和抗渗性显著提高。活性及微活性的掺合料是节约水泥,特别是节约高标号水泥的重要途径。④火山灰质接合料能加强混凝土在硫酸盐质水中的抗化学侵蚀性,提高混凝土抵抗浸析作用的抗水性,能抑制碱活性骨料反应(见混凝土甘料),防止混凝土开裂。 质t要求各种掺合料的料源选择、开采、加工、运翰、保钾、检验以及掺用工艺等都应符合质量要求,其中最基本的是材料自身质量及其掺量。主要有以下几方面:①活性水硬性掺合料的活性指标,是以19掺合料的氧化钙(CaO)吸收量(mg)表示,分为高活性、中活性和低活性3级.便用时应做材料试验鉴定。②磨细度一般与所用水泥的细度相同。③对混凝土有害的有机杂质,其烧失量不得大于规定的限值。④掺合料中的硫酸和亚硫酸化合物的含量,换算成三氧化硫(503)不应超过规定的限值。⑤非活性掺合料代替混凝土中的水泥量应按混凝土设计要求规定的限值,其28d龄期的混凝土抗压强度降低的百分数不应超过限定值。⑥非活性掺合料的掺量,应根据混凝土设计要求,限定需水量增加的百分数和坍落度减少的百分数。 掺合料的使用渗合料使用的原则是质量合格,性能适应,使用方便,成本较低等。掺用部位及最优掺t应通过试验决定。世界上有些国家主张在现场掺粉煤灰。粉煤灰是火电厂燃烧煤粉由烟道中排出的废弃粉末。其活性好,功能高,资源丰富,使用方便,是效益较优的一种接合料。粒化高炉矿渣加工困难、资源较紧缺,多数是在水泥工厂生产水泥时掺人。猫土类非活性掺合料存在需水量高、强度低、干缩量大等缺点,在水工泥凝土和钢筋混凝土中较少掺用。然而它的料源最广、价格较低,所以在要求低的或临时性工程中使用是适宜的。Chonhe}Joo掺合料(admixture)混凝土中掺人的磨细矿物材料或粉状工业废料。它是水泥的辅助材料或混凝土的填充料,可以改善混凝土性能,提高混凝土质量并节约水泥。它可以在水泥工厂粉磨水泥时掺入,如水利水电工程中广泛使用的矿渣硅酸盐水泥和火山灰质硅酸盐水泥等,就是用矿渣、火山灰、石灰石等配制的。它也可在现场拌制混凝土时掺人。 掺合料的分类分活性与非活性两类。活性掺合料水化后本身不能硬化或硬化很微弱.但可与水泥中析出的氧化钙作用,能加速混凝土凝结硬化并提高强度,粒化高炉矿渣、火山灰质材料和粉煤灰、硅粉、凝灰岩、硅藻土等都属这一类。非活性掺合料,基本上不与水泥发生化学反应,如石灰石、勃土等。 使用掺合料的目的①在粉磨水泥时掺人磨细矿物等掺合料.可大量减少水泥中的熟料量,扩大了水泥料源,降低水泥价格。②使用掺合料能改善水泥性能,增加混凝土拌和物的和易性,增加内聚力,减少离析,
  