1) ferrite magnetic pole
铁氧体磁极
2) ferrite magnet
铁氧体磁铁
3) ferrite core
铁氧体磁芯，铁氧体磁心
4) permanent ferrite
永磁铁氧体
1.
Effect of nanoadditive on the microstructure and properties of permanent ferrites;
纳米添加剂对永磁铁氧体微结构与性能的影响
2.
In order to investigate the effect of rare-earth oxide Pr6O11 on the magnetic performance of the strontium permanent ferrite and the corresponding mechanism,the sample was prepared using both BMS-4 material and Pr6O11 through milling,precipitating,forming and sintering.
为了探讨稀土氧化物Pr6O11作为添加剂对M型锶永磁铁氧体磁性能的影响及其作用机理,以添加稀土氧化物Pr6O11的BMS-4永磁铁氧体预烧料(SrFe12O19)作为原料,经过球磨、沉淀、成型、烧结等工艺制成样品。
3.
The magnetic properties of the permanent ferrite can be strongly improved by a appropriate amount of additives.
在永磁铁氧体材料中添加适量的添加剂能够极大的改善材料的磁性能。
5) permanent magnetic ferrite
永磁铁氧体
1.
In this paper, the reason for agglomeration in rotary-kiln is analyzed in production of pre-sintered permanent magnetic ferrite when the mill scale is used as raw material.
对以铁鳞为原料的烧结永磁铁氧体预烧料生产中回转窑内产生结窑块料的成因进行了分析,对实际生产中采用的改善结窑的措施和效果进行了讨论;对结窑块料的利用进行了试验研究,提出了两种解决方案,结果表明,经处理后的结窑块料,用于烧结磁粉和粘结磁粉都可以达到使用要求。
2.
The permanent magnetic ferrite was prepared by the method of solid-phase reaction with the natural magnetite without magnetic separation.
用天然磁铁矿作原料 ,不进行磁选 ,直接用固相反应法生产永磁铁氧体 。
3.
The permanent magnetic ferrite was prepared by the method of solid phase reaction with the natural magnetite without magnetic separation.
用天然铁矿作原料 ,不进行磁选 ,直接用固相反应法生产永磁铁氧体。
6) magnetic ferrite
永磁铁氧体
1.
Simulation of stress field in the sinter process of magnetic ferrite;
永磁铁氧体烧结过程应力场有限元分析
2.
Simulation of temperature field in the sinter process of magnetic ferrite;
永磁铁氧体烧结过程温度场有限元分析