1) face slab rupture
面板挤压破坏
1.
In recent years,there are some cases of concrete face slab rupture happened in several high CFRD projects.
近些年来,国内外的一些面板堆石坝工程相继出现了河床段面板挤压破坏现象,通过对面板挤压破坏机理的分析,表明造成面板挤压破坏的根本原因是堆石的变形,它与坝高、河谷形状、以及堆石的压实状况等因素有着较为密切的关系。
2) crushing rupture
挤压破坏
1.
The crushing rupture of face slab along vertical joint occurred in some newly completed concrete face rockfill dams with the height of more than 150m.
新近建成的一批坝高大于150m的面板坝的面板都发生了沿垂直缝的挤压破坏问题,因此,避免面板发生挤压破坏成为超高面板坝设计中有待解决的重大设计课题。
3) slab damage by squeezing
面板挤压破损
4) Crushing failure of ice
冰挤压破坏
5) collapsing force
挤压破坏力
1.
In order to research on the influence of moisture conditioning to mechanical characteristics,a quadratic orthogonal rotation combination designed experiment of three factors and five levels factor was carried out,the mathematical model of collapsing force was founded.
为了研究加湿调质处理对糙米力学性能的影响,采用三因素五水平二次旋转正交组合试验设计,建立糙米籽粒挤压破坏力的数学模型,分析各参数对挤压破坏力的影响规律。
6) collapse failure
挤毁破坏
补充资料：壁板挤压
壁板挤压
extrusion of panels
b iban』iya壁板挤压(extrusion of panels)壁板是一种宽且扁并带有纵向加强筋条的型材。挤压法是生产壁板的理想方法。 可用挤压法生产壁板的合金有铝合金、镁合金和钦合金，以铝合金为主。壁板主要供航空航天工业用，在舰船、车辆、特种容器、电子设备和热交换装置等方面的应用也日趋广泛。 壁板的挤压方法分实心锭坯法和空心锭坯法两种。 实心锭坯法用实心锭坯挤压平板形壁板的方法最为简单(图a)，但其主要缺点是壁板宽度受限制。壁板的宽度系数(使用圆挤压筒时)与其形状的关系如下:壁板形状-V日CC 宽度系数1 1.6 22·22·35 5 6 sd甘曝彝丽食黔 壁板挤压示意图 a一用实心图锭坯挤压平板形壁板; b一用空心圃锭坯挤压壁板管毛料 1一挤压筒;2一挤压杆，3一挤压垫. 4一锭坯，5一挤压模.6一制品;7一穿孔针 用实心圆锭坯在不同能力挤压机上挤压各种壁板的最大宽度列于表。 用实心圆锭挤压硬铝合金壁板的最大宽度圳甘庄 用扁锭坯在扁挤压筒中挤压平板形壁板是一种先进的挤压方法。用扁挤压筒挤压的平壁板宽度大约等于用圆挤压筒挤压的V型壁板的宽度.用扁挤压筒挤压壁板的最大容许宽度不受挤压机压力的限制，但受挤压机结构特点制约。用扁挤压筒可以挤压变断面壁板，壁板纵向筋条高度和形状不受限制，且纵向筋条高度实际上对壁板宽度无影响。 空心锭坯法用空心锭坯可以挤压壁板管坯(图b)，随后再把它切开、展平并矫直。用这种方法可以制造壁厚相当薄的很宽(2500mm)的壁板。在用空心锭坯挤压壁板时，容易选择适宜的挤压条件，且不受壁板横断面积和厚度的限制;可以挤压异形横断面壁板;可以采用最简单的型、棒材挤压机挤压;由于采用不润滑挤压，壁板表面质量高。缺点是:壁板宽度受到限制，不得超过挤压筒外径的30%~40%;金属流动速度较低;挤压筒使用寿命较短。