1) non-clinker cement concrete
无熟料水泥混凝土
1.
This paper discusses the qualities,composition and disposition of non-clinker cement concrete,and generalizes the project principle of making non-clinker into concrete.
论述了无熟料水泥混凝土的特点、组成及配制,通过实际操作概述了无熟料水泥混凝土的工程原理。
3) water cured concrete
水熟混凝土
4) cement without clinker
无熟料水泥
5) concrete
[英]['kɔŋkri:t] [美]['kɑŋkrit]
水泥混凝土
1.
The application of concrete in perpetual pavement;
水泥混凝土在耐久性路面中的应用
2.
Stress of asphalt overlay laying on cracked concrete pavement repaired with bridging slab;
旧水泥混凝土路面搭板罩面的应力
3.
Test research of anti-vibration performance of riving on the structure of concrete pavementsp;
水泥混凝土路面结构破釜抗振性能试验研究
6) cement concrete
水泥混凝土
1.
On the endurance of cement concrete;
浅谈水泥混凝土的耐久性
2.
Analysis on the quality control of rural cement concrete roadway construction;
简析农村公路水泥混凝土路面施工质量控制
3.
Vibration analysis on coarse aggregate gradation of interlocking-dense cement concrete;
嵌锁密实型水泥混凝土粗集料级配振动分析
补充资料：无熟料水泥
不用或使用少量硅酸盐水泥熟料作为碱性激发剂而制成的水泥。它由活性混合材料（如粒化高炉矿渣、粉煤灰、火山灰、钢渣等）和碱性激发剂（如石灰等）或硫酸盐激发剂（如石膏），按比例配合，磨细而成。
无熟料水泥一般以它所采用的原料来命名，如石膏矿渣水泥、石膏化铁炉渣水泥、石灰烧粘土水泥、石灰粉煤灰水泥、赤泥硫酸盐水泥等。生产无熟料水泥，不但主要原料可以利用工业废渣，而且激发剂也可用工业副产品，如以磷石膏、氟石膏等代替天然石膏使用。因此，生产无熟料水泥是对工业废渣或副产品和天然资源很好的综合利用。由于无熟料水泥的生产不经过生料制备和熟料烧成两道工序，因此耗能很低。无熟料水泥的水硬性、强度等性能，取决于原料的性质和配合比。这类水泥的标号一般都较低，早期强度不高，但后期强度较高，抗水性、耐蚀性和耐热性较好，而抗冻性、大气稳定性较差，易风化，不宜长期贮存。适用于地下、水中和潮湿环境中的建筑工程，也可用于制作地坪、路面以及一般建筑；不适用于冻融交替频繁、要求早期强度较高、长期处于干燥地区的建筑工程。
为改善无熟料水泥的性能，在水泥中可掺入30％以下的硅酸盐水泥熟料制成少熟料水泥(如钢渣水泥)。熟料在水泥中不但起到碱性激发剂的作用，而且还起到提高水泥早期强度，改善水泥抗冻性和抗碳化性等作用。
无熟料水泥一般以它所采用的原料来命名，如石膏矿渣水泥、石膏化铁炉渣水泥、石灰烧粘土水泥、石灰粉煤灰水泥、赤泥硫酸盐水泥等。生产无熟料水泥，不但主要原料可以利用工业废渣，而且激发剂也可用工业副产品，如以磷石膏、氟石膏等代替天然石膏使用。因此，生产无熟料水泥是对工业废渣或副产品和天然资源很好的综合利用。由于无熟料水泥的生产不经过生料制备和熟料烧成两道工序，因此耗能很低。无熟料水泥的水硬性、强度等性能，取决于原料的性质和配合比。这类水泥的标号一般都较低，早期强度不高，但后期强度较高，抗水性、耐蚀性和耐热性较好，而抗冻性、大气稳定性较差，易风化，不宜长期贮存。适用于地下、水中和潮湿环境中的建筑工程，也可用于制作地坪、路面以及一般建筑；不适用于冻融交替频繁、要求早期强度较高、长期处于干燥地区的建筑工程。
为改善无熟料水泥的性能，在水泥中可掺入30％以下的硅酸盐水泥熟料制成少熟料水泥(如钢渣水泥)。熟料在水泥中不但起到碱性激发剂的作用，而且还起到提高水泥早期强度，改善水泥抗冻性和抗碳化性等作用。