1) porous alumina
多孔型氧化铝
2) porous alumina
多孔氧化铝
1.
Preparation of porous alumina template and study on formation process;
多孔氧化铝模板的制备及形成过程研究
2.
The fabrication and transmissivity of porous alumina templates;
多孔氧化铝模板的制备及性质研究
3.
The fabrication of high-quality periodic porous alumina templates;
高质量规则多孔氧化铝模板的制备
4) porous anodic alumina
多孔氧化铝
1.
Well ordered porous anodic alumina (PAA) film was prepared on pure Al substrate using sulfuric/oxalic acid mixture as electrolyte with different ratios, the best regular PAA film with an average diameter of 45 nm was obtained using 1∶1 sulfuric/oxalic (molar concentration) mixed acid at 26 V.
高度有序的多孔氧化铝可以在3种不同类型的电解液,即硫酸、草酸和磷酸中获得。
2.
TiO_2 nanotubes were prepared by sol-gel method using porous anodic alumina as the template,and then,doped by nitrogen in ammonia gas atmosphere.
以多孔氧化铝为模板,采用溶胶凝胶法制备出二氧化钛纳米管,在氨气气氛下进行了氮掺杂。
3.
The physical structure of the porous anodic alumina was characterized by using SEM and BET.
用电化学方法制备多孔氧化铝膜,并负载Mo-Co活性组分制得了金属支撑-多孔层规整填料型加氢催化剂。
6) Porous alumina membrane
多孔氧化铝膜
1.
Nanometer-scale porous alumina membrane is prepared by anodic oxidization.
比较了电化学抛光前后铝片表面的微观结构,用阳极氧化法制备了纳米级多孔氧化铝膜,用扫描电镜研究分析了氧化铝膜孔的排列规律。
2.
Porous alumina membrane is prepared by aluminum anodizing in given acidic solution.
通过二次阳极氧化方法制备多孔氧化铝膜与一次阳极氧化方法制备多孔氧化铝膜孔排布规律性的对比 ,结果发现 ,二次阳极氧化方法制取的多孔氧化铝膜孔排布规律性明显好于一次阳极氧化法制取的多孔膜 。
补充资料：氧化铝
| 氧化铝 alumina 化学式Al2O3，白色晶状粉末。有多种变体：①自然界存在的刚玉属a-Al2O3，金属铝在氧气中燃烧 ，或将氢氧化铝灼烧至高温也能得a-Al2O3，它最稳定，熔点2015℃，沸点2980℃，密度4.0克／厘米3，莫氏硬度8.8。既不溶于水，也不溶于酸和碱，耐腐蚀和绝缘性能好，用于制造耐火材料、砂轮和绝缘材料。刚玉中因含少量杂质而显不同颜色，高温熔融得到的a-Al2O3可做人造刚玉 ，用于钟表和精密仪器的轴承及人造宝石。②将氢氧化铝或铝铵矾加热至300℃，得到γ-Al2O3，它不溶于水，能溶于酸和碱，在低温下稳定，灼烧至高温，就会转变成a-Al2O3。γ-Al2O3是一种多孔物质，具有很大的表面积，因此，它有很强的吸附能力和很高的催化活性，大量用作催化剂载体，使一些活性很高但价格昂贵的催化剂(如铂、钯等)分布在载体表面，可以减少催化剂用量，但却有很大的表面。γ-Al2O3还可做色谱分析中的吸附剂。③β-Al2O3是一种固体电解质，用于制造新型电池。④δ-Al2O3等多种变体。氧化铝的最大用途是电解法制备金属铝的原料，另外，氧化铝在陶瓷、机械、合成纤维、仪器、电子工业中也都有用途。 |