1)  ZY-type expansive agent
ZY膨胀剂
1.
Here the effect of ZY-type expansive agent used in construction of over lenth continuous mass concrete is mainly discussed.
简单介绍大体积混凝土超长无缝施工温度裂缝的控制措施,并主要讨论了ZY膨胀剂在大体积混凝土超长无缝施工中的作用。
2)  ZY high performance concrete expansive agent
ZY高性能混凝土膨胀剂
1.
In this mass concrete project, we mixed ZY high performance concrete expansive agent to make shrinkage compensating concrete, besides we adopted effective methods of warm-keeping and heat-isolation by temperature test and control, as a result, concrete crack was prevented.
大体积混凝土工程,在混凝土中掺入ZY高性能混凝土膨胀剂,配制补偿收缩混凝土,通过测温和温控,采取有效的保温隔热措施,防止了混凝土的开裂。
3)  AEA expansive agent
AEA膨胀剂
1.
This paper emphasized on the key techniques double mixing of organic short fiber in AEA expansive agent, best mixing quantities of organic short-fiber and expansive agent, restricted expansion rate after double mixing, compressive strength and bending strength of mortar etc.
本文重点论述了在AEA膨胀剂中复掺有机短纤维控制裂缝的技术关键,有机短纤维和膨胀剂的最佳掺量,复掺后的限制膨胀率,砂浆的抗压及抗折强度等技术问题。
4)  expansive agent
膨胀剂
1.
Mechanism and model of sulfate attack on RCC with expansive agent;
含膨胀剂的碾压混凝土抗硫酸盐侵蚀机理与理论模型
2.
Investigation on environmentally friendly PFA based expansive agent;
环境友好型PFA膨胀剂
3.
Some considerations on development of expansive agent and expansive concrete in china;
我国膨胀剂和膨胀混凝土的发展与问题思考
5)  expanding agent
膨胀剂
1.
Shrinkage of semi-lightweight concrete with expanding agent;
膨胀剂对次轻混凝土收缩的影响
2.
Setting compound phosphate retarder and reduced type expanding agent for building gypsum;
建筑石膏的复合磷酸盐缓凝剂及缓凝型膨胀剂
3.
To systematically study the effects of mineral admixtures such as slag,expanding agent on sulfate resistance of concrete, a series of concrete immersion test was carried out.
通过混凝土的抗硫酸盐浸泡试验,系统研究了矿渣、膨胀剂等矿物掺合料对混凝土抗硫酸盐侵蚀性能的影响。
6)  expansion admixture
膨胀剂
1.
Proper use of expansion admixture in waterproof concrete;
膨胀剂在防水混凝土中的正确应用
2.
Study on expansion admixture and steel fiber reinforcing high strength lightweight aggregate concrete;
膨胀剂与钢纤维协同增强高强轻骨料混凝土研究
3.
Influences of expansion admixture on performance of self-compacting concrete;
膨胀剂对免振捣自密实混凝土性能的影响
补充资料:静态膨胀剂破碎岩石


静态膨胀剂破碎岩石
rock breakage with static expansive agent

  定的强度。 装人炮孔中的静态膨胀剂,由于自身的膨胀作用,在孔壁的约束下,沿径向方向对炮孔壁产生较大的膨胀压力(30一soMpa)。孔壁径向受压,切向受拉,当孔径为4em,孔距为40一6oem时,软岩或混凝土产生径向破裂所需的膨胀压力为10一20MPa,中硬岩或硬岩为15一30MPa。当炮孔内的膨胀压力增加到一定值后,介质就会产生径向裂缝而破裂。 静态膨胀剂破碎岩石的效果随环境温度的提高而明显地增加。但温度过高,水化速度加快,易产生喷孔现象。为了适应环境温度的变化,控制水化速度及裂缝开裂时间,要根据环境温度采用不同配方。静态膨胀剂的吸水量,以满足化学反应(26%)或便于装灌为度,过多的水分将降低其膨胀力。 应用孔径38一42mm,孔距200~400mm,装药量1.9~2.3kg/m。其爆破lm“岩石所消耗的炸药量(下称炸药单耗)视岩石坚固性及工作状态而定,可参考下表:破碎对象孤石整体岩石素混凝土钢筋混凝土静态膨胀剂炸药单耗,kg/m33一75一126一8 15一20 静态膨胀剂操作简便,携带和运输安全,切割和破碎岩石时可做到无飞石、无震动、无冲击波、无噪声、无粉尘、无毒气排放等危害,因此可用于城市建筑物拆除、岩石基槽开挖、大块岩石的二次破碎和石料开采等工程。静态膨胀剂破碎岩石与炸药爆破相比,其缺点是作用时间长、成本较高。研究新的添加剂,缩短反应时间,提高膨胀力,降低成本为其改进方向。J ingto一pengz陌ngjl posul yansh-静态膨胀剂破碎岩石(roek breakage withstatie expansive agent)一种以氧化钙为基本成分,反应时体积膨胀,使岩石涨裂的技术。它是20世纪80年代初研究成功的非爆炸型、无公害的破碎岩石技术。可用于不允许有震动和飞石的场所,和用来开采整体石料。 作用原理静态膨胀剂以氧化钙为主要膨胀源,其含量约占81%。此外,还含有硅、铝、铁、镁的氧化物,并配以少量添加剂。在与适量水掺合后,发生水化反应,立方晶系的CaO转变成六方晶系的Ca(OH):,体积增大50.2%,同时释放出66.6kJ/mol的热量,从而具有膨胀作功的能力。有机添加剂用来延缓水化反应的速度;无机添加剂则用来控制硬结时间,并达到一
  