1) induction heating / metallic card clothing
感应加热/金属针布
2) metal card clothing
金属针布
1.
The spheroidized structure and process of 70Nb and 50Cr alloy steel wires for metal card clothing after low temperature annealing was studied.
研究了70Nb和50Cr两种金属针布合金钢丝经大塑性变形后在低温下球化退火的工艺及组织。
2.
Now the carding equipment always adapts metal card clothing.
在非织造布生产中,干法生产工艺要求必须对纤维进行梳理,非织造布梳理设备所采用的多是金属针布。
3.
80 mm special alloy steel wire for metal card clothing were studied,and their technique parameters were respectively found out.
15mmSWRH72B、金属针布专用φ3。
3) MCC
[英][,em si: 'si:] [美]['ɛm 'si 'si]
金属针布
1.
Application of Duo-servo plus CNC Punching Technology on Hi-precision MCC;
高精密金属针布双伺服数控冲齿技术的应用
4) metallic card clothing
金属针布
1.
Analysis and Discussion of Butt Welding Quality\= on New Metallic Card Clothing;
新型金属针布接头对焊质量的分析与探讨
2.
Approach to improving heat treatment quality of domestic metallic card clothing
提高国产金属针布热处理质量的途径
3.
The temperature field of metallic card clothing heated by flame during quenching process is studied by use of three-dimensional FEM analysis.
应用三维有限元方法对金属针布的火焰淬火加热进行了研究。
5) metallic clothing
金属针布
1.
On the basis of the falling behind state of the metallic clothing heat treatment technology in our country,we have designed the metallic clothing VD－MOS high frequency induction heat treatment chamber.
针对国内金属针布热处理工艺的落后状况，设计了金属针布VD－MOS高频感应热处理装置，改变了传统的热处理工艺，具有节能、加热温度均匀等优点，比国外同类产品更具有体积小、效率高的特点，从根本上革新了由电子管组成的传统高频感应加热设备。
2.
From the special experiment of card stripping on the metallic clothing carding machine,by researching the law of variation before and after card stripping on different moment we haveobtained the result which indicates that metallic clothing also need card stripping and the properperiod of card stripping is once every two days.
通过在金属针布梳棉机上专门的抄针实验，研究抄针前后不同时刻的棉结粒数的变化规律。
3.
The wear resistance of metallic clothing is an important factor influencing the quality of spinning and the productivity.
金属针布广泛用于梳棉机中,其耐磨性能对纺纱质量和生产率有很大影响。
6) Card clothing
金属针布
1.
A detailed analysis is made here on the characteristics and specifications of new card clothing as well as their nice spinning effects,the new card clothing is more effective than the obsolete ones in the reduction of cotton neps and the improvement of yarn evenness.
本文详细分析和介绍了新型金属针布的特点、规格、型号及优良的纺纱效果。
2.
The chemical component, microstructure and mechanic properties are analyzed of the local card clothing of SWRH72B, SWRH57B made by a famous manufacturer and OK40, OB20 made by Graf company in Switzerland.
本文通过对比瑞士Graf公司的OK40、OB20金属针布齿条和国内某著名针布生产企业的SWRH72B、SWRH57B金属针布齿条的化学成分、组织和性能,从材质和制备工艺方面探讨了提高金属针布耐磨性和齿条内在质量的可能性。
补充资料：金属热处理 :感应加热热处理
用感应电流使工件局部加热的表面热处理工艺。这种热处理工艺常用於表面淬火﹐也可用於局部退火或回火﹐有时也用於整体淬火和回火。20世纪30年代初﹐美国﹑苏联先后开始应用感应加热方法对零件进行表面淬火。随著工业的发展﹐感应加热热处理技术不断改进﹐应用范围也不断扩大。
基本原理 将工件放入感应器(线圈)内(图1 感应加热原理
)﹐当感应器中通入一定频率的交变电流时﹐周围即產生交变磁场。交变磁场的电磁感应作用使工件内產生封闭的感应电流──涡流。感应电流在工件截面上的分布很不均匀﹐工件表层电流密度很高﹐向内逐渐减小(图2 沿工件截面的电流密度分布
)﹐这种现象称为集肤效应。工件表层高密度电流的电能转变为热能﹐使表层的温度昇高﹐即实现表面加热。电流频率越高﹐工件表层与内部的电流密度差则越大﹐加热层越薄。在加热层温度超过钢的临界点温度后迅速冷却﹐即可实现表面淬火。
分类 根据交变电流的频率高低﹐可将感应加热热处理分为超高频﹑高频﹑超音频﹑中频﹑工频 5类。①超高频感应加热热处理所用的电流频率高达27兆赫﹐加热层极薄﹐仅约0.15毫米﹐可用於圆盘锯等形状复杂工件的薄层表面淬火。②高频感应加热热处理所用的电流频率通常为200～300千赫﹐加热层深度为0.5～2毫米﹐可用於齿轮﹑汽缸套﹑凸轮﹑轴等零件的表面淬火。③超音频感应加热热处理所用的电流频率一般为20～30千赫﹐用超音频感应电流对小模数齿轮加热﹐加热层大致沿齿廓分布﹐粹火后使用性能较好。④中频感应加热热处理所用的电流频率一般为2.5～10千赫﹐加热层深度为2～8毫米﹐多用於大模数齿轮﹑直径较大的轴类和冷轧辊等工件的表面淬火。⑤工频感应加热热处理所用的电流频率为50～60赫﹐加热层深度为10～15毫米﹐可用於大型工件的表面淬火。(见彩图 差温炉淬火
﹑ 600毫米直径冷轧辊工频感应加热淬火
﹑ 大型铸钢件的热处理炉
﹑ 真空淬火炉
)
基本原理 将工件放入感应器(线圈)内(图1 感应加热原理
)﹐当感应器中通入一定频率的交变电流时﹐周围即產生交变磁场。交变磁场的电磁感应作用使工件内產生封闭的感应电流──涡流。感应电流在工件截面上的分布很不均匀﹐工件表层电流密度很高﹐向内逐渐减小(图2 沿工件截面的电流密度分布 )﹐这种现象称为集肤效应。工件表层高密度电流的电能转变为热能﹐使表层的温度昇高﹐即实现表面加热。电流频率越高﹐工件表层与内部的电流密度差则越大﹐加热层越薄。在加热层温度超过钢的临界点温度后迅速冷却﹐即可实现表面淬火。 分类 根据交变电流的频率高低﹐可将感应加热热处理分为超高频﹑高频﹑超音频﹑中频﹑工频 5类。①超高频感应加热热处理所用的电流频率高达27兆赫﹐加热层极薄﹐仅约0.15毫米﹐可用於圆盘锯等形状复杂工件的薄层表面淬火。②高频感应加热热处理所用的电流频率通常为200～300千赫﹐加热层深度为0.5～2毫米﹐可用於齿轮﹑汽缸套﹑凸轮﹑轴等零件的表面淬火。③超音频感应加热热处理所用的电流频率一般为20～30千赫﹐用超音频感应电流对小模数齿轮加热﹐加热层大致沿齿廓分布﹐粹火后使用性能较好。④中频感应加热热处理所用的电流频率一般为2.5～10千赫﹐加热层深度为2～8毫米﹐多用於大模数齿轮﹑直径较大的轴类和冷轧辊等工件的表面淬火。⑤工频感应加热热处理所用的电流频率为50～60赫﹐加热层深度为10～15毫米﹐可用於大型工件的表面淬火。(见彩图 差温炉淬火
﹑ 600毫米直径冷轧辊工频感应加热淬火 ﹑ 大型铸钢件的热处理炉 ﹑ 真空淬火炉 ) 说明：补充资料仅用于学习参考，请勿用于其它任何用途。