2) warm compaction technology
温压成形技术
3) forming technology
成形技术
1.
Research into magnesium alloy forming technology and its developing status quo;
镁合金成形技术的研究和发展现状
2.
Investigation and applications of forming technology of magnesium alloy and foamed magnesium alloy;
镁合金及泡沫镁合金成形技术的开发与应用
3.
Development of superplasticity and forming technology of magnesium alloys
镁合金超塑性及其成形技术进展
4) Forming technique
成形技术
1.
Presents a forming technique of a full-sized two-dimensional nozzle with infrared suppression and analyzes the forming technique of a test sample.
研究全尺寸红外抑制二元喷管的成形技术，并对试验件的成形工艺作了分析。
2.
Lightweighting design,the relationship between the performances of auto parts & components and the property parameters of materials,and the application of advanced forming technique are also elaborated.
论述了汽车轻量化的意义、表征参量、评价方法、实施路径和方法;轻量化的设计,零部件和构件的功能与材料性能参量的关系以及先进成形技术的应用。
6) n ear-net shaping technique
近净形成形技术
补充资料：主要射出成形材料成形时应注意事项
■主要射出成形材料成形时应注意事项
品 名 注 意 事 项
PVC
聚氯乙烯
1. 产品种类范围非常广（硬质、软质、聚合物等），成型条件各有不同，从熔融至分
解之温度范围很小，尤须注意加热温度。
2. 附着水分少，但成型周期尽可能减少（50℃~60℃热风干燥）。
3. 成型机方面，与材料直接接触的部位须电镀或采用不锈钢以防热分解所产生的盐酸
侵蚀。射出压力2100kg/cm2程度。
4. 所有塑料当中必须是细心注意温度调节。
5. 浇口附近易产生流纹，故射出操作后，柱塞不要后退使浇口充分固化后再瞬间退后为宜。
6. 加热之初温不宜高，特别注意熔融情形。第二级加热温度较高，且尽可能使成形周
期缩短，比较安全。
PA
聚醯胺树脂
1. 成型温度比其它材料高，故采用油加热的成形机较适当。
2. 吸湿性大，必须充分干燥。水分对成型品的品质影响甚大（80℃热风干燥约5~6小时）。
3. 须退火以消除内部歪斜。
PP
聚丙烯
1. 同PE，但成形温度必须较高。熔融温度170℃，超过190℃则流动性大增，则毛边增加，
易产生接缝及凹入情形。
PC
聚碳酸脂
1. 吸湿性比尼龙小，但若有些微之水分存在则成型品产生其它色泽或气泡，故必须密封
干燥同时成形时也须预备干燥（120℃之温度4小时）。
2. 加热温度超过320℃时则产生热分解，成品变色，故特别注意温度调节，又成型时的温度调节也非常重要，须特别注意其最低温度、最低时间。
3. 须退火以消除内部歪斜（130℃~135℃，1小时程度为准）。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。