1) Nano adhesion
纳米粘着力
2) nano-clay
纳米粘土
1.
Study on Nano-clay Toughened Epoxy Resin;
纳米粘土增韧环氧树脂的研究
2.
Based on a large amount of publications,the process of dispersing nano-clay into epoxy resin and preparation methods of nano-clay/epoxy composites in our country are introduced.
通过对大量文献的调研,介绍了国内纳米粘土的分散方法及其改性环氧树脂复合材料的制备方法,着重对影响纳米粘土改性环氧树脂复合材料性能的主要因素进行了综述。
3.
By orthogonal analysis, the nano-clay was the montmorillonite intercalated by HDTMAB, get across impact experiment make know, when feedback temperature 90℃、montmorillonite content 5%、 feedback time 2h was best condition.
采用正交方案,蒙脱石通过HDTMAB阳离子插层制备纳米粘土,冲击实验表明最佳条件为:反应温度90℃、矿浆浓度5%、反应时间2h。
3) Nanoclay
纳米粘土
1.
Research progress in preparation and application of nanoclay
纳米粘土的制备及应用研究进展
2.
At the present,nanoclay/polymer composites are the focus of research on materials science due to their superior properties.
纳米粘土 /聚合物复合材料因其具有优异的性能是目前材料科学研究的热点 。
4) adhesion
[英][əd'hi:ʒn] [美][əd'hiʒən]
粘着力
1.
The contact mechanics model is established and the relation of the adhesion to the normal forces is simulated.
以JKR接触理论和GW粗糙表面模型为基础,将聚氨酯表面与光滑蓝宝石球的接触作为点接触,与玻片的接触看做是多个凸峰与光滑平面的接触,建立接触力学模型分析粘着力与法向力间的关系。
2.
When the ratio of polyol and diphenylem-thanediisocyanate is 1:2, the adhesion between rough surface and samples reaches its maximum.
结果表明,聚氨酯的化学成分对其粘着性能有重要影响,在多羟基化合物与MDI(二异氰酸酯)的组分比为1:2时,粘着力最大。
3.
For the special robot's foot design based on imitating the gecko's foot, the characteristics of adhesion and friction of 4 samples of polyurethane were tested.
结果表明,负法向力(即粘着力)随法向力的增加而呈对数规律增加;在负法向力下,切向力随负法向力的增加而线性增加;在一定负法向力下,切向力随初始法向力的增加按对数规律增加。
5) Adhesive Force
粘着力
1.
A formula of active earth pressure on retaining wall was proposed which considers the cohesion force on sliding plane and the adhesive force on interface of soil and retaining wall.
考虑滑裂面上填土的粘聚力及填土与墙背接触面上的粘着力,推得了粘性填土挡墙上的主动土压力计算公式。
2.
Based on the numerical method for the contact of wheel and rail with a water medium, a numerical method of analyzing the adhesive force between high speed wheel and rail with a water medium is developed under the condition of neglecting the part of traction forces transferred by the water medium.
借助于水介质作用下轮轨接触的数值解法 ,在忽略了由水介质传递的轮轨牵引力的条件下 ,建立了高速轮轨水介质粘着力的数值分析方法。
3.
in this paper, the generating principle of the tractive force and the brake power as well as their relationship to the adhesive force are analysed based on the mechanics theory.
本文根据力学原理分析了牵引力和制动力产生的机理，以及两者与粘着力的关系，得出牵引力和制动力的相同与不同之处，并提出应试验研究“计算最大制动力的粘着系数计算公式”。
6) adhesion force
粘着力
1.
The causes to dropping of the adhesion force at high speed are analyzed.
分析了高速时粘着力下降的原因 ,介绍了国外高速车辆改善粘着、提高粘着力的方法 ,提出我国高速车辆应采取的相应措
2.
The main feature of the model is the incorporation of the particle adhesion force and the large deformation of the particle and pad.
基于芯片/磨粒/抛光垫的微观接触力平衡关系,建立了考虑抛光垫/磨粒大变形和粘着力效应的微观接触模型。
补充资料：看纺织印染中应用纳米材料和纳米技术
纺织印染中应用纳米材料和纳米技术时，除了要解决纳米材料的制备技术之外，重要的是要解决好纳米材料的应用技术，其中关键问题是使纳米粒子和纺织印染材料的基本成分（即聚合物材料）之间处于适当的结合状态。印染中，纳米粒子在聚合物基体中的分散和纳米粒子在聚合物表面的结合是主要的应用技术问题。 制备聚合物/无机纳米复合材料的直接分散法，适用于各种形态的纳米粒子。印染中纳米粒子的使用一般采用直接分散法。但是由于纳米粒子存在很大的界面自由能，粒子极易自发团聚，利用常规的共混方法不能消除无机纳米粒子与聚合物基体之间的高界面能差。因此，要将无机纳米粒子直接分散于有机基质中制备聚合物纳米复合材料，必须通过必要的化学预分散和物理机械分散打开纳米粒子团聚体，将其均匀分散到聚合物基体材料中并与基体材料有良好的亲和性。直接分散法可通过以下途径完成分散和复合过程： 高分子溶液（或乳液）共混：首先将聚合物基体溶解于适当的溶剂中制成溶液（或乳液），然后加入无机纳米粒子，利用超声波分散或其他方法将纳米粒子均匀分散在溶液（或乳液）中。有人将环氧树脂溶于丙酮后加入经偶联剂处理过的纳米TiO2，搅拌均匀，再加入 40wt%的聚酰胺后固化制得了环氧树脂/TiO2纳米复合材料。还有人将纳米SiO2粒子用硅烷偶联剂处理后，改性不饱和聚酯。 熔融共混：将纳米无机粒子与聚合物基体在密炼机、双螺杆等混炼机械上熔融共混。如将PMMA和纳米SiO2粒子熔融共混后，双螺杆造粒制得纳米复合材料。又如利用偶联剂超声作用下处理纳米载银无机抗菌剂粒子，分散制得PP/抗菌剂、PET/抗菌剂、PA/抗菌剂等复合树脂，然后经熔融纺丝工艺加工成抗菌纤维。研究表明，将经过表面处理的纳米抗菌剂粒子通过双螺杆挤出机熔融混炼，在聚合物中可以达到纳米尺度分散，获得了具有良好综合性能的纳米抗菌纤维，对大肠杆菌、金黄色葡萄球菌的抗菌率达到95%以上（美国AATCC－100标准）。 机械共混：将偶联剂稀释后与碳纳米管混合，再与超高分子量聚乙烯（UHMWPE）混合放入三头研磨机中研磨两小时以上。将研磨混合物放入模具，热压，制得功能型纳米复合材料。 聚合法：利用纳米SiO2粒子填充（Poly（HEMA））制备了纳米复合材料。纳米SiO2粒子首先被羟乙基甲基丙烯酸（HEMA）功能化，然后与HEMA单体在悬浮体系中聚合。还有利用SiO2胶体表面带酸性，加入碱性单体4－乙烯基吡咯进行自由基聚合制得包覆型纳米复合材料。