1) polycarbosilane microspheres
聚碳硅烷微球
2) polysiloxane microspheres
聚硅氧烷微球
1.
The polysiloxane microspheres varied from 2 μm to 9 μm as light scattering agents were dispersed in acrylate resin to get a coating solution.
将粒径为2~9μm的聚硅氧烷微球作为光散射剂均匀分散于丙烯酸树脂中,涂布于厚度为180μm的聚对苯二甲酸乙二醇酯(PET)薄膜表面,挥发溶剂制得光散射薄膜。
3) Polycarbosilane
聚碳硅烷
1.
The curing process for polycarbosilane fiber with cyclohexene vapor;
聚碳硅烷纤维在环己烯气氛中的不熔化处理
2.
SiC fiber with a low oxygen content prepared by polycarbosilane fiber cured in 1-hexyne vapor;
聚碳硅烷纤维在1-己炔气氛中不熔化处理制备低氧含量SiC纤维
3.
Synthesis and structure characterization of phenyl-containing polycarbosilane.;
含苯基聚碳硅烷的合成与结构分析
4) PCS
聚碳硅烷
1.
Study on the viscosity of PCS/xylene solution;
聚碳硅烷/二甲苯原液粘度特性的研究
2.
Selection of the Solvent in PCS Nanoparticle Preparation Process by Gas Antisolvent Recrystallization;
抗溶剂气体重结晶制备聚碳硅烷纳米微粒的溶剂选择
3.
Modified SiC absorbents were obtained by pyrolyzing polycarbo silane (PCS) mixed with Ni and Co nano metal powder up to 1 000℃ and in N 2 medium, and its pyrolyzation behaviors were investigated by TG and IR analysis.
在聚碳硅烷先驱体中掺混Ni、Co等纳米金属微粉 ,在N2 气氛中裂解至 10 0 0℃ ,得到改性碳化硅吸收剂。
5) polycarbosilane(PCS)
聚碳硅烷
1.
A continuous polycarbosilane(PCS) multifilament was melt spun at≈300℃.
通过改变不同的熔融纺丝工艺研究了聚碳硅烷纤维熔融纺丝时纺丝稳定性的影响因素。
2.
Trilobal polycarbosilane(PCS) fibers were prepared by melt spinning PCS precursor through Y shaped spinneret.
以聚碳硅烷 (PCS)为原料 ,采用熔融纺丝制备三叶型 PCS纤维后 ,经不熔化和烧成制得三叶型碳化硅纤维。
3.
The application of chromium(Cr) in the preparation of polycarbosilane(PCS) derived ceramics was investigated.
研究了活性填料铬 (Cr)在聚碳硅烷 (PCS)先驱体裂解陶瓷中的应用。
6) super fine polysiloxane microspheres
超细聚硅氧烷微球
补充资料：十八烷氧基封端二甲基(硅氧烷与聚硅氧烷)
CAS：68554-53-0
中文名称：十八烷氧基封端二甲基(硅氧烷与聚硅氧烷)
英文名称：Siloxanes and Silicones, di-Me, (octadecyloxy)-terminated
中文名称：十八烷氧基封端二甲基(硅氧烷与聚硅氧烷)
英文名称：Siloxanes and Silicones, di-Me, (octadecyloxy)-terminated
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条