1) castings material
铸件材质
3) quality of cast iron
铸铁材质
4) quality of casting
铸件质量
1.
Production experience has showed that quality of casting has be.
通过对油压机横梁、汽轮机缸体、油轮挂舵臂和宽厚板轧机机架等一些特大型铸钢件的生产,实践表明:采用有机酯水玻璃砂后,铸件质量明显提高,铸件气孔、裂纹减少,表面光洁,尺寸精度提高。
5) casting quality
铸件质量
1.
The effect of reservoir on casting quality in dental high frequency casting;
齿科高频铸造中储金球对铸件质量的影响
2.
This result was obtained by the casting quality enhancing of key parts such as crankshaft, cylinder block and head.
时风ZS1115H型单缸发动机达到欧Ⅱ排放标准,得益于发动机关键零部件如曲轴、缸体、缸盖铸件质量的提升,而铸件质量的提高则主要依靠先进铸造技术和检测方法的应用,其中包括:自动化造型线造型、热芯盒制芯、覆砂铁型铸造、曲轴等温淬火和氮化、光谱快速分析等。
3.
0 and Microsoft Graph 2000 Software,the data management and analysis system for compacted graphite iron casting quality was established.
该系统建立了九类铸件质量数据分类管理的数据库 ,能快速、准确地进行添加、查询、修改和删除数据 ;利用柱形图等图形工具直观地显示数据统计分析的结果 ;能够快速、方便地生成各类不同格式的报表。
6) high quality casting
优质铸件
1.
Getting high quality casting depends on mature and stable technology and management of production.
优质铸件是靠成熟而稳定的生产工艺、生产管理来保证的,不同时期它又随着新技术、新材料、新工艺的不断涌被现而赋于新的质量标准。
补充资料:SECC材质标准
SECC材质标准
1.主题
本标准规定了我司用电镀锌薄碳钢带SECC的技术要求。
*本标准适用复押工艺和滚压工艺生产用SECC。
2.引用标准
GB223 钢铁及合金化学分析方法
GB228 金属拉伸试验方法
GB230 金属洛氏硬度试验方法
GB232 金属弯曲试验方法
GB2975 钢材力学及工艺性能试验取样规定
GB4156 金属杯突试验方法
3.分类
标记形式::SECC-„D T##´##(#表示数字,”´”之前表示厚度,之后表示
宽度。单位mm)
举例:SECC-SD T0.6´33.9表示厚度0.6mm宽度33.9mm的电镀锌薄碳钢带。
4.技术要求
*4.1化学成分
元素代号
C
Si
Mn
P
S
百分含量%
<0.12
<0.05
<0.50
<0.025
<0.025
钢中其他残余元素含量应符合下列规定:
Cu<0.15%, Ni<0.15%, Cr<0.15%, As<0.05%, Sn<0.05%.
4.2拉伸性能
抗拉强度
屈服强度
下列厚度(mm)的伸长率 %
MPa
MPa
0.25~<0.4
0.4~<0.6
0.6~<1
1<1.6
1.6~<2.5
³2.5
300~400
250~320
³32
³34
³36
³37
³38
³40
4.3硬度
代号
S
8
4
2
1
HRB
45~55
50~71
65~80
76~85
³85
*HV
<100
95~130
说明:补充资料仅用于学习参考,请勿用于其它任何用途。