1) electrical arc erosion
电弧烧损
2) arc ablation
电弧烧蚀
1.
For improving the arc ablation resistance of nozzle materials of high-voltage circuit breaker,it is needed to fill Al 2 O 3 and TiO 2 in PTFE to reduce the ablation of arc energy and improve the arc ablation resistance of nozzle.
为了提高高压断路器喷口材料的耐电弧烧蚀性能,采用在聚四氟乙烯(PTFE)中添加三氧化二铝或二氧化钛,降低电弧能量对PTFE的烧蚀,同时试验研究复合聚四氟乙烯介电性能的变化规律。
3) arc erosion
电弧烧蚀
1.
It is found by XRD that the phase structure of La2NiO4 ceramics did not change after arc erosion and exhibited a high chemical stability.
X射线衍射分析发现La2NiO4陶瓷在电弧烧蚀作用下相结构不发生变化,具有高的化学稳定性。
2.
After cryogenic treatment,the resistance property of arc erosion of CuCr50 vacuum contact material change dramatically.
CuCr50真空触头材料经深冷处理后 ,抗电弧烧蚀性能明显提高。
3.
The samples of carbon sliding panel infiltrated with copper were prepared,and the friction test and arc erosion test were carried out.
制备了浸铜碳滑板试样,并通过试验研究了浸金属碳滑板和纯碳滑板的机械摩擦性能与电弧烧蚀性能。
6) electrode erosion
电极烧损
1.
Research on electrode erosion mechanisms in water vapor plasma arc;
水蒸气等离子弧电极烧损机理的研究
2.
The mechanism of electrode erosion has been studied by the correspondence tests between scanning electorn micrograghs of the ends of the electrodes and the losing weights of them.
通过空气等离子切割电极烧损量与电极端面电镜形貌的对应试验,探讨了电极烧损机理。
补充资料：烧损
烧损
fire waste
Sh0OSUn烧损(fi re waste)钢在高温状态下因氧化而造成的损耗。从锭坯到成品的整个生产过程中钢要经过多次加热，据测定，每加热一次约有0.5%一2.5%的钢被烧损。烧损不仅造成钢的直接损失，产生的氧化铁皮还降低钢的导热能力，侵蚀炉底耐火材料，恶化炉子操作条件，对轧件顺利咬入和钢材表面质量也产生不良影响。因此，减少金属烧损是钢加热过程中的重要间题。钢的烧损(氧化)过程主要是铁与炉气中的C02、02、H20发生化学反应的过程，其反应式如下: Fe+粤。，一Feo 2-‘一_ 3Fe+202一一Fe3O- ZFe:04+今。:一3FeZo3 -一‘一”’2一‘-一‘一J Fe+CO:一FeO+CO 3Fe+4COZ一Fe3O4+4CO 3FeO+COZ一FesO;+CO Fe十HZO一FeO+HZ 3Fe+4HZO一Fe3O4十4H2 3Fe+HzO一-今Fe3O;+Hz烧损与加热温度、加热时间、炉内气氛和钢的化学成分等因素有关。加热温度越高、高温下停留的时间越长、炉内氧化性气氛愈浓，则加热时的烧损愈多。因此减少烧损的主要措施是，在满足加热工艺的条件下，适当提高加热速度，缩短加热时间;控制炉内气氛，在保证燃料完全燃烧的条件下，减少过剩的空气并防止冷空气的吸入等。此外，采取保护性气体或用保护性涂料也能减少或防止钢的氧化。 (衷康)
说明：补充资料仅用于学习参考，请勿用于其它任何用途。