1) polyurethane potting material
聚氨酯的应用灌封材料
2) polyurethane pouring sealant
聚氨酯灌封料
1.
High performance polyurethane pouring sealant was prepared with polytetramethylene glycol(PTMG),totylene diisocyanate(TDI) and methylene bis ortho chloroaniline(MOCA) solution,and the effects of the equivalent ratio n (—NH 2)/ n (—NCO), w (—NCO),finished cure time and relative humidity on the mechanical and electric properties were investigated.
以聚四甲撑醚二醇、甲苯二异氰酸酯和ＭＯＣＡ 溶液为原料，采用半预聚体法合成了高性能聚氨酯灌封料。
3) polyurethane grouting material
聚氨酯灌浆材料
4) polyurethane material
聚氨酯材料
1.
The development of rubber & plastics seals in material modified and modern version composition elastomer and progress in research and application of low fraction material, polyurethane material, thermoplastic elastomer and nanocomposites were summarized.
综述了近年来橡塑密封在材料改性、新型复合弹性体的开发 ,低摩擦、自润滑材料、聚氨酯材料、热塑性弹性体以及纳米复合材料等方面的研究应用进展。
5) urethane potting resin
聚氨酯封装料
6) encapsulating material
灌封材料
1.
Study on modified epoxy resin-encapsulating materials
改性环氧树脂灌封材料的研制
2.
Milled glass fiber (MG)/polyurethane (PU)/epoxy resin (EP) encapsulating material was prepared by vacuum priming.
采用真空灌注工艺,制备磨碎玻璃纤维(MG)／聚氨酯(PU)／环氧(EP)灌封材料,并对其力学性能和微观结构进行研究。
3.
Epoxy resin/nano-silica encapsulating materials were obtained from in situ polymerization, and microstructure and properties of the materials were investigated by transmission electron microscopy(TEM),scanning electron microscopy(SEM) and differential scanning calorimetry(DSC).
采用原位聚合法制备了环氧树脂/纳米S iO2灌封材料。
补充资料：电力电容器灌封料
分子式：
CAS号：
性质：树脂(A)为聚醚填充料等，固化剂(B)为改性异氰酸酯等。由聚醚与辅助材料经脱水精制后再加填充料和催化剂进行反应，然后经研磨混合、过滤而成。树脂为白色或黄色黏液。密度1.35～1.40g/cm3。黏度(25℃)7000mPa·s左右。固化剂为黑色或黄色黏液。密度1.10～1.15g/cm3，黏度(25℃)5500mPa·s左右。用于电容器元件特别适用于电力电容器的表面密封和固定。
CAS号：
性质：树脂(A)为聚醚填充料等，固化剂(B)为改性异氰酸酯等。由聚醚与辅助材料经脱水精制后再加填充料和催化剂进行反应，然后经研磨混合、过滤而成。树脂为白色或黄色黏液。密度1.35～1.40g/cm3。黏度(25℃)7000mPa·s左右。固化剂为黑色或黄色黏液。密度1.10～1.15g/cm3，黏度(25℃)5500mPa·s左右。用于电容器元件特别适用于电力电容器的表面密封和固定。