1) manganese copper zinc nanocrystalline ferrite
锰铜锌纳米晶铁氧体
2) ZnMn ferrite nanoscale particles
锌锰铁氧体纳米晶
3) nanocrystal MnZn ferrite particle
锰锌铁氧体纳米晶
1.
Single phase aggregate-free nanocrystal MnZn ferrite particles with a size of 10～20nm were perapared via hydrothermal method by additive, which were characterized by TEM and XRD.
通过加入添加剂经水热合成法制备了单相无硬团聚的 10～ 2 0nm锰锌铁氧体纳米晶 ,运用TEM ,XRD等进行了表征。
4) nano-sized Mn-Zn ferrite powders
纳米锰锌铁氧体
1.
Based on the precursor of ZnSO 4 ·7H 2 O,FeCI 3 ·6H 2 O and MnSO 4 ,nano-sized Mn-Zn ferrite powders were synthesized by the catalysis of Fe 2+ in boiling circumfluence.
以ZnSO4·7H2O,FeCl3·6H2O和MnSO4为原料,采用液相沸腾回流法,成功地制备出了纳米锰锌铁氧体。
5) MnZn ferrite nanocrystal
锰锌铁氧体纳米粉体
1.
The MnZn ferrite nanocrystal has been successfully synthesized by a simple synthesis, co-precipitation phase transformation.
本文采用的软磁锰锌铁氧体纳米粉体,是用一种简单的方法,即共沉淀沸腾回流相转化法制备的。
6) nano-size NiZnCu(Cr)-ferrite
纳米镍锌铜(铬)铁氧体
补充资料：锰-锌铁氧体
分子式：Mn-Zn
CAS号：
性质：软磁铁氧体的主要品种之一。具有尖晶石型结构。密度5.1g/cm3，维氏硬度600～800。初始磁导率ua1000～5000。磁导率与品质因素的乘积150000(100kHz)。居里点134～200℃。饱和磁感应强度0.3～0.5T。矫顽力8～36A/m。电阻率20～1000Ω·cm。主要原料为铁、锰、锌的氧化物或盐类。一般用电子陶瓷工艺制造。如采用控制气氛烧结或热压烧结等新工艺，可获得性能优良的产品。一般在1kHz～10MHz频率范围内使用。可用于制作电感器、脉冲变压器、滤波器的磁芯、介质天然及磁头等。
CAS号：
性质：软磁铁氧体的主要品种之一。具有尖晶石型结构。密度5.1g/cm3，维氏硬度600～800。初始磁导率ua1000～5000。磁导率与品质因素的乘积150000(100kHz)。居里点134～200℃。饱和磁感应强度0.3～0.5T。矫顽力8～36A/m。电阻率20～1000Ω·cm。主要原料为铁、锰、锌的氧化物或盐类。一般用电子陶瓷工艺制造。如采用控制气氛烧结或热压烧结等新工艺，可获得性能优良的产品。一般在1kHz～10MHz频率范围内使用。可用于制作电感器、脉冲变压器、滤波器的磁芯、介质天然及磁头等。