1) silver tin oxide contact material
AgSnO2触点材料
2) AgSnO 2 electric contact material
AgSnO2电触头材料
1.
Compared with the same conventional materials,AgSnO 2 electric contact material made by high-pressure oxidation technique processes had great improvement in electrical properties.
与常规AgSnO2电触头材料相比 ,采用高压氧化技术及工艺制造的AgSnO2电触头材料的电性能有很大改
3) AgSnO2 materials
AgSnO2材料
4) AgSnO2 composite
AgSnO2复合材料
5) contact materials
触点材料
1.
And factors affecting electric erosion,such as circuit parameters,mechanical parameters,contact materials working surroundings,etc.
叙述了触点的分合过程,说明了熔桥产生和电弧引燃的原因;介绍了直流条件下触点材料的转移机理,包括熔桥转移和极性转移;还介绍了影响电侵蚀的多种因素,例如:电气参数、机械参数、触点材料、环境因素等。
2.
According to the present study of contact materials and the existing problems in these fields, we put forward a new notion to work on those materials and turn out a kind of Ag_based conductive ceramic contact materials to meet the application demands in low_voltage transformer industry.
针对目前触点材料领域的现状和存在的问题及低压电器对触点材料的应用要求 ,提出了一种研究触点材料的新思路 ,制成了银基导电陶瓷触点材料。
3.
Investigated is the effect of industrial environment on surface corrosion and electrical behaviors of several contact materials (gold, nickel and tin plating).
针对常用连接器触点材料(镀金、镀镍、镀锡),研究工业环境对其表面的腐蚀性及对触点微动电特性的影响。
6) contact material
触点材料
1.
The service performance of three kinds of contact materials by powder metallurgical (AgCdO(10), AgSnO2 (10) and AgYb2 O3 (12)) was studied in 20 A 20 V DC loading condition, such as contact resistance, welding force and material transfer.
以粉末冶金法制备的AgCdO(10)、AgSnO2(10)、AgYb2O3(12)三种银金属氧化物触点材料为研究对象,在DC20V、20A,纯阻性负载条件下,研究其电气性能,包括接触电阻、熔焊力与材料转移。
2.
The development, qualities, applications and technics of the contact materials was reviewed in this paper and the development trends of contact material and the problems for all kinds of it to be solved are present as well.
本论文综述了触点材料的发展现状、特性、应用及工艺研究,描述了触点材料的发展趋势及其要解决的问题。
补充资料：银-金属氧化物触点材料
分子式：
CAS号：
性质：银基含有镉、锌、锡、铟、铜等金属元素的合金，经过内氧化处理，各添加元素变成金属氧化物弥散在银基体中，从而提高了银合金的使用寿命。有Ag-12CdO-1T，Ag-15CdO-1T，Ag-10ZnO-1T，Ag-6SnO2-4In2O3-1T 和Ag-10SnO2-4In2O3-1T等合金。布氏硬度分别为690～1225MPa、740～1265MPa、740～1265MPa、720～1255MPa和820～1325MPa；电阻率分别为3.4μΩ·cm、3.5μΩ·cm、3.5μΩ·cm、3.3μΩ·cm和3.5μΩ·cm。熔炼-压力加工及冲压成型-内氧化方法，或粉末冶金-压力加工-冲压成型方法制造。主要作各种低压开关电器的触点(T添加元素)。
CAS号：
性质：银基含有镉、锌、锡、铟、铜等金属元素的合金，经过内氧化处理，各添加元素变成金属氧化物弥散在银基体中，从而提高了银合金的使用寿命。有Ag-12CdO-1T，Ag-15CdO-1T，Ag-10ZnO-1T，Ag-6SnO2-4In2O3-1T 和Ag-10SnO2-4In2O3-1T等合金。布氏硬度分别为690～1225MPa、740～1265MPa、740～1265MPa、720～1255MPa和820～1325MPa；电阻率分别为3.4μΩ·cm、3.5μΩ·cm、3.5μΩ·cm、3.3μΩ·cm和3.5μΩ·cm。熔炼-压力加工及冲压成型-内氧化方法，或粉末冶金-压力加工-冲压成型方法制造。主要作各种低压开关电器的触点(T添加元素)。