1) density of A vacancy
A缺位浓度
1.
The density of A vacancy [VA] depends on how A site and B site displaced by M3+.
A缺位浓度[VA]取决于M3+的A位或B位取代情况，M3+只取代A位[（Sr,Ca）1-xMx（VA）x/2]TiO3,或M3+只取代B位[（Sr,Ca）1-x/2（VA）x/2]（Ti1-xMx）O3,产生A缺位浓度[VA]较大，对其瓷料介电性能影响较明显；M3+同时取代A和B位[（Sr,Ca）]1-x1Mx1]（Ti1-x2Mx2）O3，由于电价补偿，产生A缺位浓度[VA]较小，因而对其瓷料介电性能影响较小。
2) oxygen vacancy concentration
氧离子缺位浓度
3) Defect concentration
缺陷浓度
1.
The paper has proved that when the defect production velocity and the temperature of the thermostat, the controllable parameters,are in some range, there are the defect concentration and temperature oscillate periodically with time-the time dissipative str.
采用线性化处理、拓扑映射及数值计算相结合的方法，求解了离子辐照下各向同性晶体薄片中缺陷浓度和温度满足的非线性微分方程组，证明了当可控参量，即缺陷产生速度和恒温箱温度处于某些范围时。
2.
The results of positron annihilation spectra showed that defect concentration was different in all the DLC films.
对在不同极板负偏压下采用射频-直流等离子体方法制备得到的类金刚石膜(a-C:H)的微结构进行了测量,利用慢正电子束实验装置,探测并分析了样品缺陷浓度的分布情况。
4) concentration of point defects
点缺陷浓度
5) Vacancy concentration
空位浓度
1.
Effect of Vacancy Concentration on Elastic Property in Aluminum under High Pressures;
高压下空位浓度对金属铝弹性性质的影响
2.
Molecular Dynamics method and EAM potential are used to simulate the effect of vacancy concentration on elastic constants of aluminum under high pressures.
对6×6×6、7×7×7、8×8×8、9×9×9各失去一个原子的4种含有不同空位浓度的铝系统的弹性系数进行了模拟,并对同一浓度的缺陷晶体在0~15GPa压强范围的弹性系数进行了计算,发现空位浓度的提高降低了铝的弹性系数,而压强的增大使得缺陷系统的弹性系数越接近相同压强完整晶体的弹性系数。
3.
The results showed that the vacancy concentration was a function of concentration of element and bonding energy of the element.
结果表明 ,合金元素结合的空位浓度的大小与合金元素的浓度、合金元素与空位的结合能有直接的关系 ,Li的加入使得合金中其它元素所占有的空位浓度减小 ,两种试验合金均析出了细小、弥散分布的沉淀相 ,其原因是由于Li原子捕获了不少空位 ,使得Zn、Mg原子的进一步扩散与聚集受到限制 ,η′(MgZn2 )相的长大速度减慢 ,计算结果为试验结果提供了理论依
6) Institutional Absence
制度缺位
1.
Institutional Absence:the Internal Factor of Affecting the Effectiveness of Quality Education——According to the View of the New Institutional Economics;
制度缺位:影响素质教育有效性的内在因素——基于新制度经济学视角