1) Zn-Ti doped Ba-ferrite
Zn-Ti替代钡铁氧体
2) substituted Ti-Mn-barium ferrite
替代Ti-Mn-钡铁氧体
3) Zn ferrite
Zn铁氧体
1.
Nanocrystalline Zn ferrite was prepared by high energy ball milling.
用高能球磨法制备了纳米晶Zn铁氧体通过样品的Mossbauer谱及XRD谱的测定，研究了纳米晶的形成过程结果表明：球磨约3hα-Fe2O3即与ZnO发生机械化学反应生成Zn铁氧体，这种反应是通过先形成α-Fe2O3-ZnO固溶体而进行的。
2.
Nanocrystalline Zn ferrite,synthesized by hig h energy ball milling from ZnO+α-Fe2O3 powder mixture,exhibited non-normal spinel structure and ferrimagnetism (σs=16.
通过高能球磨方法由α-Fe2O3+ZnO混合粉体制得的Zn铁氧体纳米晶具有非正型分布的尖晶石结构,表现为亚铁磁性,其比饱和磁化强度σs=16。
4) zinc ferrite
Zn铁氧体
1.
2 K to RT, showing that their magnetic ordering took place at a much higher temperature than that of bulk zinc ferrite.
用固相反应法制备了大块的 Zn Fe2 O4 ,用聚乙烯醇 ( PVA)溶胶凝胶法制备出 6～ 90 nm的 Zn Fe2 O4 纳米微粉 ,用 X衍射研究了 Zn铁氧体纳米颗粒的结构 。
5) barium ferrite
钡铁氧体
1.
Study on the synthesis and electromagnetic properties of polyaniline-barium ferrite composites;
聚苯胺/钡铁氧体复合材料制备及电磁性能研究
2.
A study on dispersion behavior of barium ferrite in enthanol;
钡铁氧体在乙醇中分散行为的研究
3.
Effects of Bi2O3 doping on the mcrostructure and high-frequency magnetic properties of low-temperature sintered Co-Ti substituted barium ferrites;
Bi_2O_3对低烧Co-Ti替代钡铁氧体显微结构与高频磁性的影响
6) barium hexaferrite
钡铁氧体
1.
Development of study on nanophase barium hexaferrite absorber;
纳米钡铁氧体吸波材料的研究进展
2.
In this paper, the preparation methods of utrafine barium hexaferrite powders were studied, including cryochemical method, spay drying method, chemical coprecipitation method, hydrothermal synthesis, glass crysrallization, micromulsion mediated process, metal organic method, organic resin method, self-propagating high-temperature synthesis and supercritical fluid drying method, et al.
综述了近年来在M型(磁铅石结构)钡铁氧体超微粉体合成领域的一些研究进展,包括低温化学法、喷雾热解法、化学共沉淀法、水热法、玻璃晶化法、微乳液法、金属有机物水解法、有机树脂法、自蔓延高温合成法、溶胶-凝胶法等。
3.
Hexagonal plateshaped barium hexaferrite was directly synthesized by using ferrous chloride (FeCl2) as a starting material at 230 °C.
用FeCl2,BaCl2·2H2O,KNO3作为前驱体溶液,在230°C水热直接合成六角片状钡铁氧体,降低了钡铁氧体的合成温度。
补充资料：钡铁氧体类塑料磁体
分子式：
CAS号：
性质：指以钡铁氧体磁性粉末与高分子材料复合构成的复合型高分子磁性体。钡铁氧体是由α型Fe2O3与锶的氧化物通过烧结制成，属于新型稀土磁性材料。与塑料等高分子材料复合后构成永久性磁体，其磁能积可以达到相当高的水平。其应用领域与锶铁氧体类塑料磁体相同。
CAS号：
性质：指以钡铁氧体磁性粉末与高分子材料复合构成的复合型高分子磁性体。钡铁氧体是由α型Fe2O3与锶的氧化物通过烧结制成，属于新型稀土磁性材料。与塑料等高分子材料复合后构成永久性磁体，其磁能积可以达到相当高的水平。其应用领域与锶铁氧体类塑料磁体相同。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条