1) criteria of high-speed run-in
快速磨合规范
2) running-in specifications
磨合规范
1.
The new running-in specifications of transmission,having the strengthening effect,was estimated by the results of strengthening under low amplitude load of single tooth bending of cylindrical gear.
根据国产某变速箱倒挡圆柱齿轮低载强化的试验结果,制定了对变速器具有强化效果的新磨合规范,并在新磨合规范下进行了试验研究。
2.
By measuring the topographies of inner surfaces of diesel cylinders, the author carried out a study on the current running-in specifications of Dongfeng 4B diesel locomotive engine through simulation tests.
采用检测表面形貌的方法 ,通过模拟试验对东风4B型内燃机车柴油机的现行磨合规范进行试验研究 ,研究分析磨合进展情况 ,提出改进的磨合规范 ,并在实际使用的机车柴油机上做实测性试验 ,检测磨合前后柴油机缸套内表面的表面形貌的变化 ,以判断“改进磨合规范”合理程度。
3) running-in criterion
磨合规范
1.
Research on Diesel Engine Running-in Criterion Based on Oil Monitoring Techniques;
基于油液监测的D6114柴油机磨合规范研究
4) cold running-in criterion
冷磨合规范
1.
Condition-based cold running-in criterion of engine based on the variation pattern of reverse drive torque;
基于反拖扭矩变化发动机视情冷磨合规范研究
5) mechanism of high-speed run-in
快速磨合机理
1.
It has also made an inquiry into the run-in criterion and described the mechanism of high-speed run-in.
应用铁谱分析方法对ＣＳ４９２Ｑ－１Ａ汽车发动机的快速磨合过程进行了试验分析，对其磨合规范进行讨论，并阐述了其快速磨合机理。
6) rapid erosion
快速磨损
1.
Mechanism of rapid erosion failure in CFB boilers;
循环流化床锅炉快速磨损失效机理
补充资料：磨合
在机器装配后使用前，为了使配合件正常稳定运转的一种措施，也称跑合。磨合是一种有意安排的磨损过程。机械零件的磨损过程一般包括磨合阶段、稳定磨损阶段和剧烈磨损阶段(见图)。OA为磨合阶段。机器开动后，磨损率(即OA曲线的斜率)从大逐渐减小。这是由于摩擦副表面微观凹凸不平，开始时实际接触面积很小,接触应力很大。在磨合过程中,较软的零件表面材料发生塑性流动，使接触面积扩大并出现加工硬化层。对于较硬材料，高的微凸体被磨去，表面逐渐变得平坦而使接触面积增加。这些变化使以后的磨损率减小而达到磨合目的。磨合应由轻到重缓慢加载，并保持润滑油的清洁，防止磨屑进入摩擦面而造成剧烈的磨损和发热。在磨合过程中须严密注意运转情况（听声、测温等）。磨合结束后应仔细清洗并换用新的润滑油。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。