1)  aluminium silicate fiber containing zirconia
含锆硅酸铝纤维
1.
The fabrication of aluminium silicate fiber containing zirconia strengthening electronic ceramic body composites was carried out .
以电瓷坯料为基体,以含锆硅酸铝纤维为增强体,分别在1240℃、1250℃、1260℃及1270℃下制备了纤维加入量不同的电瓷复合材料。
2)  alumina zirconate fiber
锆酸铝纤维
3)  zirconfibre,zirconiumsilicatefibre;
硅酸锆纤维
4)  silicon carbide fibers containing zirconium
含锆碳化硅纤维
5)  aluminum silicate fibers
硅酸铝纤维
1.
Al2O3-SiO2/AZ91D magnesium matrix composites with compacted structure were prepared with aluminum silicate fibers and AZ91D magnesium alloy by squeeze casting method.
采用硅酸铝纤维和镁合金制备出结构紧密的Al2O3-SiO2/AZ91D镁基复合材料。
2.
Specific to difficult for aluminum silicate fibers into paper and intensity of the paper is not high,Through a series of experiments researched on carboxyl methyl cellulose (CMC),modified polyvi- nyl alcohol (PVA),cationic starch are commonly used on adhesive,which effected on aluminum silicon fibers into paper,performance of strength.
针对硅酸铝纤维难成纸且成纸强度不高的问题,本文通过一系列实验研究了羧甲基纤维素(CMC)、改性聚乙烯醇(PVA)、阳离子淀粉(CS)三种常用胶粘剂对硅酸铝纤维成纸、增强性能的影响。
6)  aluminum silicate fiber
硅酸铝纤维
1.
The application of boric acid modified phenolic resin in aluminum silicate fiber paper
硼酸改性酚醛树脂在硅酸铝纤维纸中的应用
2.
To solve the low strength problem of silica aerogel,the nanoporous super insulation materials,reinforced with aluminum silicate fiber,were prepared from TEOS through sol-gel process and supercritical drying technology.
为解决SiO2气凝胶质脆的难题,以正硅酸乙酯为硅源,采用溶胶-凝胶法和超临界干燥工艺制备了硅酸铝纤维增强纳米孔超级绝热材料,容重为74~189 kg。
3.
Flexible micro-porous calcium silicate insulation material is composed of porous spherical agglomerates consisting of many tiny needlelike xonotlite crystals and aluminum silicate fiber,most part of which has been formed flexible ceramic fiber paper before formation of the insulation material.
微孔硅酸钙柔性隔热材料由以硬硅钙石针状微小晶体构成的微孔硅酸钙球形颗粒和硅酸铝纤维复合而成,其中大部分硅酸铝纤维首先形成柔软的纸型材料,微孔硅酸钙颗粒和其余硅酸铝纤维沉积其上,填充在硅酸铝纤维之间的大孔隙中。
补充资料:含铬硅酸铝耐火纤维


含铬硅酸铝耐火纤维
alumina-silicate-chrome refractory fibre

hangeguisuanlu naihuox一a附e-含铬硅酸铝耐火纤维(a lumina一silica加chr-omerefraetory fibre)含er:033%~6纬的高纯硅酸铝纤维隔热耐火材抖。这类纤维的化学成分为:Aho:+510:+Cr:03大于99%,其中倪(AhO:+Cr203):m(5102)勺1:1。 制造含铬硅酸铝纤维的基本原理是基于CrZO3能改善Al:03一510:系玻璃相的性质,抑制玻璃相析晶,并能阻止晶粒长大。Cr:0,还能阻止纤维伺的烧结作用,提高纤维的使用温度。中国从19”年开始研制,1981年批量生产。 含铬硅酸铝耐火纤维的生产工艺与高纯硅映铝衬火纤维基本柑同.采用工业氧化铝、硅石、三氧化二铬(Cr203>98%)作原料,按一定的比例配料、混合、制成团块、用电炉熔化,喷吹法成纤. 含铬硅酸铝耐火纤维的荃本性能为:Al刃:+5102+erZo3大于99写(其中erZo:s%一6%),Fe,03小于0.3%,K:O+Na:0小于0.4%。纤维直径2~6“m,渣球含量小于5%,加热线收缩(1400℃,6h)2·8%一3.3%,热导率(热面温度1000℃,冷面盆度559℃)0.093W/(m·K)。 含铬硅酸铝耐火纤维的最高使用温度为1400℃,长期使用温度为1200℃。当在1200℃以上使用时,CrZO3的挥发速度加快,易失去Cr20:的作用。在1375℃加热保温25h,完全析晶,平均晶枚尺寸为0.3脚,保温100h,晶粒长大至。.5料m.析出的晶体多数为莫来石,少量方石英。方石英在加热和冷却过程中发生晶形转变,使纤维结构破坏。Cr:O:挥发物对人体有害,因此,含铬纤维已逐渐被其他高温耐火纤维代替。 (王全相)