1) modified fine cement
改性细水
1.
The material characteristics of modified fine cement and the labo-ratory in-situ grouting test results with different water-cement ratioes of grout was analysed and discussed in this paper.
通过对改性细水泥的材料性能、不同水灰比浆体室内试验及现场灌浆试验成果断分析和讨论,说明水灰比对岩体可灌性有很大的影响,低水灰比灌浆可明显改善灌浆效果,据高岩体的可灌性。
2) GGBS modified micro-fine cement
磨细矿渣改性超细水泥
3) polymer modified superfine cement
聚合物改性超细水泥
5) property alteration through superfine processing
超细改性
6) hydrothermal modification
水热改性
1.
Effect of hydrothermal modification conditions on preparation of flame retardant Mg(OH)_2 in large-scale experimental set-up;
水热改性条件对制备氢氧化镁阻燃剂中试研究的影响
2.
Preparation of dispersive zinc oxide nano-particles via hydrothermal modification route
水热改性法制高分散纳米氧化锌工艺初探
3.
The hydrothermal modification behavior of industrial Mg(OH)_(2) products in a new additive solution was researched.
研究了氢氧化镁工业品在一种新型添加剂作用下的水热改性行为,考察了添加剂体系、反应温度、反应时间、添加剂浓度和填充度等因素对水热产物的影响,并用扫描电子显微镜(SEM)、X射线衍射(XRD)和激光粒度仪等对水热产物进行了表征。
补充资料:染料细粉及超细粉
分子式:
CAS号:
性质:非水溶性染料或不易溶染料常采用的剂型。如分散染料、还原染料等对粒度及粒度分布均有一定要求,要求相对集中,过细、过粗,均对使用有不良影响。染料生产企业对本企业的产品均作了规定。这些染料产品一般多在2μm到上到4μm范围内,如对某些分散染料要求控制在1μm左右,分散性能4~5级,还原染料也与分散染料近似,故有超细粉之称。为使染料产品达到上述细度,常采用万能粉碎机或砂磨、球磨等进行粉碎。
CAS号:
性质:非水溶性染料或不易溶染料常采用的剂型。如分散染料、还原染料等对粒度及粒度分布均有一定要求,要求相对集中,过细、过粗,均对使用有不良影响。染料生产企业对本企业的产品均作了规定。这些染料产品一般多在2μm到上到4μm范围内,如对某些分散染料要求控制在1μm左右,分散性能4~5级,还原染料也与分散染料近似,故有超细粉之称。为使染料产品达到上述细度,常采用万能粉碎机或砂磨、球磨等进行粉碎。
说明:补充资料仅用于学习参考,请勿用于其它任何用途。
参考词条