1) phosphate polyoxyethylene nonylphenol
壬基酚聚氧乙烯醚磷酯酯
1.
The content of mono-ester,di-ester and phosphoric acid in phosphate polyoxyethylene nonylphenol were reported with mixed-solvents by potentiometric titration.
采用混合溶剂 ,用电位滴定法测定壬基酚聚氧乙烯醚磷酯酯中单酯、双酯、磷酸的含量。
2) polyoxyethylene nonylphenol phosphoric potassium
壬基酚聚氧乙烯醚磷酸酯钾盐
1.
The results show that the content of polyoxyethylene nonylphenol phosphoric potassium.
以壬基酚聚氧乙烯醚(NP-4)为原料合成了壬基酚聚氧乙烯醚磷酸酯钾盐,用电位滴定法测定了单双酯的含量,并分别用于催化乙氧基化反应。
3) phosphate polyoxyethylene nonyl phenol
壬基酚聚氧乙烯醚磷酸酯
1.
Synthesizing and properties of phosphate polyoxyethylene nonyl phenol;
壬基酚聚氧乙烯醚磷酸酯的合成及性能研究
4) Phosphated, ethoxylated nonylphenol
聚氧乙烯壬基酚磷酸酯
5) polyoxyethylene nonyl phenyl ether succinate
壬基酚聚氧乙烯醚琥珀酸酯
1.
The influences of kinds of catalyst, molar of raw materials, and other reaction conditions on the reaction were studied on the basis of the synthesis method of polyoxyethylene nonyl phenyl ether succinate using polyoxyethy-lene nonyl phenyl ether and maleic anhydride as raw materials.
在原有合成壬基酚聚氧乙烯醚琥珀酸酯方法的基础上,讨论了催化剂种类、原料配比及其他反应条件对反应的影响,确定了壬基酚聚氧乙烯醚琥珀酸酯的最佳合成条件:催化剂为自制催化剂,原料摩尔比1。
6) polyoxycthylcne nonylphcnol olcatc
壬基酚聚氧乙烯醚油酸酯
补充资料：聚酚酯
分子式：
CAS号：
性质： 又称聚酚酯、芳香族聚酯树脂，是全芳香族饱和聚酯树脂的简称。由所有羟基和羧基直接连在芳核上的单体制得的聚酯。品种较多，且以共聚酯为多。商品名为U-聚合物的即是。系白色粉末或浅黄色粒料。相对密度1.21；拉伸强度71MPa，伸长率8％～50％，悬臂梁(1zed)缺口冲击强度220J/m；热变形温度(1.82MPa)170℃，连续使用温度-70～180℃；介电强度30MV/m，介电常数(106Hz)2.62，体积电阻率3×1016Ω·cm。由双酚A钠盐与苯二甲酰氯界面缩聚或溶液缩聚制得。可在较高温度下注塑、挤塑。它是典型的高性能工程塑料。主要用作机械、电子、汽车零部件，医疗器械；耐高温管材、板材和绝缘薄膜。也可用作耐高温纤维和胶黏剂的原料。
CAS号：
性质： 又称聚酚酯、芳香族聚酯树脂，是全芳香族饱和聚酯树脂的简称。由所有羟基和羧基直接连在芳核上的单体制得的聚酯。品种较多，且以共聚酯为多。商品名为U-聚合物的即是。系白色粉末或浅黄色粒料。相对密度1.21；拉伸强度71MPa，伸长率8％～50％，悬臂梁(1zed)缺口冲击强度220J/m；热变形温度(1.82MPa)170℃，连续使用温度-70～180℃；介电强度30MV/m，介电常数(106Hz)2.62，体积电阻率3×1016Ω·cm。由双酚A钠盐与苯二甲酰氯界面缩聚或溶液缩聚制得。可在较高温度下注塑、挤塑。它是典型的高性能工程塑料。主要用作机械、电子、汽车零部件，医疗器械；耐高温管材、板材和绝缘薄膜。也可用作耐高温纤维和胶黏剂的原料。
说明：补充资料仅用于学习参考，请勿用于其它任何用途。
参考词条